为满足用户对钢中磷含量的要求,攀钢采用"双渣法"转炉脱磷工艺开展脱磷试验,并根据生产条件和转炉工艺特点考察转炉脱磷专用氧枪的实际使用效果。试验中,转炉工艺冶炼前期低温脱磷,后期脱碳升温,吹炼前期采用低供氧强度脱磷喷枪,倒渣时切换为常规吹炼喷枪。在吹炼脱磷前期结束扒渣后,熔池中的w([P])下降至0.040%以下,脱磷率为47.9%。在试验终点钢水中的w([P])均在0.010%以下,波动范围在0.006%~0.010%,w([P])的平均值是0.0081%。终点脱磷率波动范围是84.4%~92%,平均值是88.3%。

In order to satisfy the requirements of consumers on phosphorus content in steel,dephosphorization tests using double slag dephosphorization method in BOF were carried out in Pangang Group Company Ltd.,as well as investigation on actual use effects of BOF dephosphorization special oxygen lance according to production conditions and process features of BOF.During the tests,dephosphorization was done at the earlier low temperature stage and decarbonization which led to higher temperature was done at the later stage.The special oxygen lance with low oxygen supply was used at the earlier stage and then was replaced by the routine oxygen lance in the later deslagging period.Phosphorus content in steel had dropped to below 0.040% and the dephosphorization ratio was 47.9% after slagging-off while dephosphorizing prior period finished.At the end of BOF,w([P]) had declined to less than 0.010%,waving in the range from 0.006% to 0.010%,and the average w([P]) was 0.0081%.Dephosphorization ratio was between 84.4% and 92% at the BOF end and for the average of 88.3%.

参考文献

[1] 郭宏海,宋波,毛璟红,赵沛.冷却速率对耐候钢中磷元素宏观偏析的影响[J].炼钢,2010(04):55-59.
[2] 徐文杰,李安东,刘国勇.复吹转炉冶炼X65管线钢脱磷工艺研究[J].上海金属,2009(04):21-24.
[3] Yuji Ogawa;Masataka Yano;Shinya Kitamura et al.Develop- ment of the Continuous Dephosphorization and Deearbonization Process Using BOF[J].Tetsu To Hagane-Journal of the Iron & Steel Institute of Japan,2001,87(01):21.
[4] Pham Khanh SON;Yoshiaki KASHIWAYA .Phosphorous Partition in Dephosphorization Slag Occurring with Crystallization at Initial Stage of Solidification[J].ISIJ International,2008(9):1165-1174.
[5] 杨文远,郑丛杰,杨立红,陈华,崔健,许春雷,蒋晓放.大型转炉炼钢脱磷的研究[J].炼钢,2002(01):30-34.
[6] 高文芳,陈钢,王金平,姜茂发,钟良才.顶底复吹转炉高效脱磷研究[J].钢铁,2009(09):36-41.
[7] 李建新,郝旭东,仇圣桃,赵沛.复吹转炉多功能法脱磷工艺[J].北京科技大学学报,2009(08):970-973.
[8] Somnath BASU;Ashok Kumar LAHIRI;Seshadri SEETHARAMAN .Change in Phosphorus Partition during Blowing in a Commercial BOF[J].ISIJ International,2007(5):766-768.
[9] Norifumi Asahara;Ken-ichiro Naito;Itsuro Kitagawa.Fundamental Study on Interaction Between Top Blown Jet and Liquid Bath[A].Sydney:The University of New South Wales,2010
[10] 潘秀兰,王艳红,梁慧智,冯士超.国内外转炉脱磷炼钢工艺分析[J].世界钢铁,2010(01):19-21,41.
[11] 康复,陆志新,蒋晓放,钟志敏.宝钢BRP技术的研究与开发[J].钢铁,2005(03):25-28.
[12] 黄希祜.钢铁冶金原理[M].北京:冶金工业出版社,2004
[13] Monaghan B J;Pomfret R J.The Kinetics of Dephosphoriza- tion of Carbon-Saturated Iron Using an Oxidizing Slag[J].Metallurgical and Materials Transactions B:Process Metallurgy and Materials Processing Science,1998(29):111.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%