以α-丁基-ω-|3-[2-羟基-3-(N-甲基-N-羟乙胺基)丙氧基]丙基|聚二甲基硅氧烷和α,ω-双[3-(1-甲氧基-2-羟基-丙氧基)丙基]聚硅氧烷为原料,合成了聚硅氧烷接枝和嵌段改性聚氨酯水分散体,考察了改性方法及加料顺序对水性聚氨酯胶膜性能的影响.结果表明,在聚硅氧烷含量相同的条件下,胶膜的耐水性和耐溶剂性,接枝改性试样优于嵌段改性的试样,前加料方式的试样优于后加料的试样.透射电镜显示水分散体中分散相颗粒的形状随聚硅氧烷用量的增加变得更不规则,扫描电镜图片表明,接枝改性的试样相分离程度更明显.
参考文献
| [1] | Victor Bulacovschi;Vladimir Condratov .Thermal stability and the tensile properties of some segmented poly(ester-siloxane)urethanes[J].Polymer Degradation and Stability,1999(2):259-265. |
| [2] | 戴家兵,张兴元,李维虎,葛震,冯林林,许戈文.新型水分散有机硅-聚氨酯共聚物的结构与性能[J].高分子材料科学与工程,2007(03):122-125. |
| [3] | Zhu XL;Zhang M;Zhang QS;Feng SY;Kong XZ .Synthesis and characterization of bis(methoxyl hydroxyl)-functionalized disiloxane and polysiloxane oligomers derivatives therefrom[J].European Polymer Journal,2005(9):1993-2001. |
| [4] | Chen RS;Chang CJ;Chang YH .Study on siloxane-modified polyurethane dispersions from various polydimethylsiloxanes[J].Journal of Polymer Science, Part A. Polymer Chemistry,2005(16):3482-3490. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%