在铁片试样上研究以次磷酸钠为还原剂的化学镀Ni-Fe-Ru-P合金镀层的工艺,考察了金属盐浓度对化学镀反应沉积速率的影响.利用优化的工艺配方在经过敏化,活化处理后的纳米碳纤维表面沉积Ni-Fe-_Ru-P合金镀层,分别利用EDS、XRD、SEM等手段对镀层的成分,结构,形貌进行了表征,并对其进行了热处理.结果表明,利用化学镀技术可以在纳米碳纤维表面获得连续、均匀的Ni-Fe-Ru-P合金镀层,且镀层为非晶态结构.在350℃以下热处理不会改变镀层的结构,在400℃以上热处理,镀层开始晶化.
参考文献
| [1] | SMITH G V;BROWER W E;MATYJASZCZYK M S.Metallic glasses:New catalyst systems[A].Amsterdam:Elsevier Press,1981 |
| [2] | VAN WONTERGHEM J;MφRUP S;KOCH C J W et al.Formation of ultra-fine amorphous alloy particles by reduction in aqueous solution[J].NATURE,1986,322(6080):622-623. |
| [3] | 曾平莉,江玲超,周莉.负载型非晶态合金催化剂的制备[J].浙江化工,2009(06):9-13. |
| [4] | T.N.Rostovshchikova;V.V.Smirnov;S.A.Gurevich;V.M.Kozhevin;D.A.Yavsin .Nanostructured metal films:Fabrication and catalytic properties[J].Catalysis Today,2005(3/4):344-349. |
| [5] | Jing Fang;Xueying Chen;Bo Liu;Shirun Yan;Minghua Qiao;Hexing Li;Heyong He;Kangnian Fan .Liquid-phase chemoselective hydrogenation of 2-ethylanthraquinone over chromium-modified nanosized amorphous Ni-B catalysts[J].Journal of Catalysis,2005(1):97-104. |
| [6] | 孙开莲.非晶态合金催化剂研究进展[J].滁州学院学报,2007(03):62-64. |
| [7] | 任吉丽,韩长秀,张宝贵.非晶态合金催化剂研究[J].天津化工,2007(01):1-4. |
| [8] | 李庆伟,周春晖,蔡晔,葛忠华.非晶态合金催化剂的研究综述[J].化工生产与技术,2001(06):30-33. |
| [9] | 吕志果,郭振美.负载型非晶催化剂制备及应用技术新进展[J].工业催化,2003(02):46-49. |
| [10] | 刘全夫,宋华,李锋,李玉华.非晶态合金催化剂的研究进展[J].当代化工,2005(03):210-213. |
| [11] | Guangwen Xie;Wei Sun;Weibing Li .Synthesis and catalytic properties of amorphous Ni-Co-B alloy supported on carbon nanofibers[J].Catalysis Communications,2008(3):333-335. |
| [12] | Guangwen Xie;Zhiguo Lu;Zhaobo Wang .Synthesis and catalytic properties of amorphous Ni-P alloy hollow microspheres[J].Catalysis Communications,2008(8):1766-1769. |
| [13] | 毕韶丹.化学镀Ni-Co-P合金的工艺控制因素[J].表面技术,2004(04):46-47. |
| [14] | 李宁;屠振密.化学镀实用技术[M].北京:化学工业出版社,2004 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%