利用差示扫描量热仪、偏光显微镜和万能材料试验机等研究了不同成核剂用量对聚甲醛MC90的结晶行为和力学性能的影响。结果表明,成核剂的加入可有效减小POM的球晶尺寸,提高POM的结晶温度和缺口冲击强度。当成核剂添加量为0．8%时,最大结晶温度由139．2℃提高到143．3℃,球晶平均尺寸约60μm,为未加成核剂的POM 球晶尺寸的1/2,缺口冲击强度由5．5kJ·m-2增加到6．1kJ·m-2。
Effects of the different dosage of nucleator on crystallizing and mechanical property of POM were stud-ied by means of differential scanning calorimetry,polarizing microscopy and universal material testing machine. The results indicated that nucleators effectively decreased spherocrystal size of POM. And the nucleators could improve crystallization temperature and notched impact strength. When the addition amount was 0. 8%,it made crystalliza-tion peak temperature of POM increased from 139. 2℃ to 143. 3℃, spherocrystal size decreased to 1/2 of POM without nucleator,and notched impact strength was improved from 5. 5kJ·m-2 to 6. 1kJ·m-2.
参考文献
| [1] | 方伟;杨玮婧;孟永智;李丽英.复合光稳定剂对共聚甲醛光老化性能的影响[J].现代塑料加工应用,2015(5):41-43. |
| [2] | 孙建丽;胡友亮;叶林;刘廷华.聚甲醛结晶性能的改性[J].塑料工业,2006(7):19-21. |
| [3] | 冯清正;姜立忠;孙长江;潘小君;胡维斌.新型成核剂对聚甲醛树脂结构与性能的影响[J].工程塑料应用,2014(5):105-108. |
| [4] | 王亮亮;陈科宇;商亚东;薛长青;操斌;付玉娥.成核剂对聚甲醛结构与性能的影响[J].工程塑料应用,2013(6):84-87. |
| [5] | 徐卫兵;朱士旺;蔡琼英.均聚甲醛对共聚甲醛成核作用的研究[J].中国塑料,2000(3):39-42. |
| [6] | 王亮亮;陈科宇;刘慧宏;吴桂波;商亚东;薛长青;操斌;陈步宁.聚甲醛结晶成核剂研究进展[J].塑料工业,2012(9):5-9,22. |
| [7] | 张凌;顾有伟;胡艳芳.聚甲醛成核剂对其结构和性能的影响研究[J].塑料,2004(2):43-45. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%