A new type of hot-rolled transformation induced plasticity (TRIP) steel with 2.3%Al was developed to replace conventional Si-bearing TRIP steel to improve surface quality of the steel sheet. The relationship between retained austenite volume fraction and hot-rolling processing was researched by Gleeble-2000 thermo-dynamic test for the Al-bearing steel. The experimental result showed that aluminum played an important role on retaining austenite and the volume fraction increased from 4.4% to 7.5% as coiling temperature increased from 350℃ to 450℃, while coiling temperature had a stronger effect on retaining austenite than finishing rolling temperature.