为改变高硼中碳合金钢中硬质相的形态和分布,在高硼中碳合金钢凝固过程中施加电压1 600V、频率30 Hz、脉宽不同的电脉冲,并研究了电脉冲脉宽对其凝固组织的影响规律.结果表明,经过电脉冲处理,高硼中碳合金钢凝固组织中马氏体片层间距变小,基体中W、Cr、Mo、V等合金元素含量升高,基体硬度提高；硬质相体积分数降低,片层状硬质相消失,网状硬质相产生断网现象,硬质相形态和分布也变得均匀.随着电脉冲脉宽的增加,断网现象先变得明显,后又减弱.在该试验条件下,脉宽为30 μs时,断网现象最明显,硬质相的分布和形状也最均匀.
参考文献
| [1] | JIANG Ye-hua;ZHOU Rong-feng;ZHOU Rong et al.Microstructures and Properties of a Bainite and Martensite DualPhase Cast Steel Fabricated by Combination of Alloying and Controlled Cooling Heat Treatment[J].Materials Science Forum,2005,475/479(01):93. |
| [2] | Asoka K Misra .A Novel Solidification Technique of Metals and Alloys:Under the Influence of Applied Potential[J].Metallurgical and Materials Transactions,1985,16A(07):1354. |
| [3] | Conrad H;Sprecher A F .Dislocations in Solids[J].Acta Crystallographica Section A:Foundations of Crystallography,1989,45(07):499. |
| [4] | Nakada M;Shiohara Y;Flemings M C .Modification of Solidification Structure by Pulse Electric Discharging[J].ISIJ International,1990,30(01):27. |
| [5] | Hummel R E .Electromigration and Related Failure Mechanisms in Intergrated Circuit Interconnects[J].International Materials Reviews,1994,39(03):97. |
| [6] | 秦荣山 .电脉冲作用下的非平衡转变研究[D].中国科学院金属研究所,1996. |
| [7] | 何树先,王俊,孙宝德,周尧和.高密度脉冲电流对过共晶Al-Si合金凝固组织的影响[J].中国有色金属学报,2002(02):275-278. |
| [8] | 王建中,齐锦刚,杜慧玲,刘铁铮,苍大强.电脉冲孕育处理对纯铝凝固组织的影响[J].材料科学与工艺,2008(05):646-649. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%