In this paper,the high strength room temperature blackening film on steel surface were prepared, the structure and the forming principle of the film were studied. The Cu-Se-P system with high strength composition blackening was researched, and the factors that affect the wear resistance of the film were analyzed. The experiment shows that the procedure have many advantages, such as short treatment time, high efficiency, low cost, high adhesive strength, perfect wear resistance, which posed a new approach for blackening of machine parts.