以SWRS82B钢为研究对象,制定热处理工艺:将试样奥氏体化后在低温盐槽停留短时间后马上进入高温盐槽等温,目的是增加珠光体转变过冷度,提高珠光体形核率,减小珠光体团尺寸,从而探索高碳珠光体钢力学性能与显微组织尺寸之间的关系.结果表明,珠光体钢强度指标主要由珠光体片层间距决定.晶粒尺寸明显影响塑性指标,晶粒尺寸越小塑性指标越高,而当晶粒尺寸相近时,珠光体团尺寸越细小断面收缩率越高.
参考文献
| [1] | 蔡爱国 .铌钒微合金中碳钢的微观组织与强度的关系[J].钢铁研究学报,1996,8(02):35-39. |
| [2] | W.J.Nam;C.M.Bae .Effect of interlamellar spacing on cementite dissolution during wire drawing of pearlitic steel wires[J].Scripta materialia,2000(5):457-463. |
| [3] | 李翔,康永林,顾克井,魏军,陈银莉,蔡开科.铌微合金化高碳钢的连续冷却转变[J].钢铁研究学报,2004(03):44-48. |
| [4] | Elwazri AM;Wanjara P;Yue S .The effect of microstructural characteristics of pearlite on the mechanical properties of hypereutectoid steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):91-98. |
| [5] | Akhmad A. Korda;Y. Mutoh;Y. Miyashita .Effects of pearlite morphology and specimen thickness on fatigue crack growth resistance in ferritic-pearlitic steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):262-269. |
| [6] | 王燕,方峰,王雷,蒋建清,杨恒.冷拔珠光体钢丝渗碳体微观结构[J].材料热处理学报,2010(05):92-95. |
| [7] | 涂益友 .高速大应变冷拔钢丝的组织和力学性能[D].东南大学,2006. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%