采用热力学计算、光学显微镜(OM)、扫描电镜(SEM)、能谱分析(EDS)等方法,分析研究了GH4700合金铸锭的显微组织及元素偏析情况,并研究了均匀化温度与时间对合金元素再分配的影响规律.结果表明:GH4700合金铸锭存在严重的枝晶偏析,Nb、Ti等元素大量偏聚于枝晶间,主要的析出相为γ'相、Laves相、MC碳化物及少量的δ相,热力学计算结果与实际相符；在均匀化过程中,元素发生明显的再分配,随着温度升高和保温时间的延长,Ti、Nb元素逐渐扩散均匀,当热处理制度为1170℃×48 h时,元素偏析基本消除,有害析出相回溶,是可选的均匀化工艺.
参考文献
| [1] | Zhao S Q;Xie X S;Gaylord D Smith et al.Research and improvement on structure stability and corrosion resistance of nickel-base superalloy INCONEL alloy 740[J].Materials & Design,2006,27(10):1120-1127. |
| [2] | Christopher J. Cowen;Paul E. Danielson;Paul D. Jablonski .The Microstructural Evolution of Inconel Alloy 740 During Solution Treatment, Aging, and Exposure at 760℃[J].Journal of Materials Engineering and Performance,2011(6):1078-1083. |
| [3] | 龙正东;马培立;仲增墉 .IN706合金锭的均匀化处理[J].钢铁研究学报,1997,9(01):21-24. |
| [4] | 仲增墉,庄景云.变形高温合金生产工艺中几个重要问题的研究和进展[J].钢铁研究学报,2003(z1):1-9. |
| [5] | Semiatin S L;Kramb R C;Turner R E et al.Analysis of the homogenization of a nickel-base super alloy[J].Scripta Materialia,2004,491:51-52. |
| [6] | 田玉亮,王玲,董建新,张麦仓.GH742铸锭偏析及均匀化过程中元素分布规律[J].稀有金属材料与工程,2006(08):1315-1318. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%