为探讨磁致冷材料Gd表面溅射保护膜后的附着性能,利用直流磁控溅射技术在Gd基体上镀不锈钢(1Cr18Ni9Ti)薄膜.采用扫描电镜(SEM)﹑能谱仪﹑扫描探针显微镜对薄膜进行了表征,并用引拉法测定了薄膜的附着强度.结果表明,不锈钢薄膜溅射初期呈岛状分布;溅射一定时间后薄膜呈层状生长,表面质量好,膜/基界面结合好,附着强度高,在功率密度为966W/cm2、溅射时间为8min时附着强度达到最大值24.7MPa.
参考文献
| [1] | Zimm C;Jastrab A;Gschneidner Jr K et al.Description and performance of a near-room temperature magnetic refrigerator[J].Advances in Cryogenic Engineering,1998,43(05):1957. |
| [2] | 吕学超,鲜晓斌,汪小琳,郎定木,刘清和.离子轰击镀对铀上铝镀层组织及防腐蚀性能的影响[J].中国腐蚀与防护学报,2003(05):299-303. |
| [3] | 庞晓轩,沈保罗,尹昌耕.铀及铀合金防护镀层的研究进展[J].材料导报,2007(01):72-74. |
| [4] | Sanchette F .Mechanically reinforced and corrosion-resistant sputtered amorphous aluminum alloy coatings[J].Surface Technology,1998,98(1-3):1162. |
| [5] | Brazzle JD;Taylor WP;Ganesh B;Price JJ;Bernstein JJ .Solution hardened platinum alloy flexure materials for improved performance and reliability of MEMS devices[J].Journal of Micromechanics and Microengineering,2005(1):43-48. |
| [6] | 王庆富,刘清和,王晓红,郎定木,李科学,唐凯,刘卫华.磁控溅射离子镀铌贫铀的电化学腐蚀行为[J].稀有金属材料与工程,2008(02):289-293. |
| [7] | 杨勇,吴卫,郑小秋.表面溅射保护膜对Gd腐蚀行为的影响[J].材料保护,2006(09):7-9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%