Alloying structural steel used for mechanical structures has a high requirement for cleanliness because its failures are greatly affected by non-metallic inclusions and total oxygen content in steel.It has been reported by some steelmaking plants to have some problems in controlling total oxygen content and inclusions during alloying structural steel production.For this purpose,cleanliness control in 0.2C-0.3Si-0.6Mn-1Cr-0.2Mo steel was investigated.Firstly,low melting temperature zone（≤1873 K） of CaO-Al2O3-MgO system and formation condition of low melting temperature inclusions were investigated through thermodynamic equilibrium calculation.On this basis,industrial tests were carried out.Through sampling at different stages,transformation of oxide inclusions and change of total oxygen content in steel were studied.The results show that：in order to form CaO-Al2O3-MgO system inclusions with low melting temperature,mass percent of Al2O3,MgO and CaO in inclusions should be controlled from 37.6% to 70.8%,0 to 17.4% and 25.5% to 60.6%;For the condition of 1873 K and 0.05%（mass percent） dissolved aluminum in steel,the activities of dissolved oxygen,magnesium and calcium should be controlled as 0.298×10-4-2×10-4,0.1×10-5-40×10-5 and 0.8×10-8-180×10-8 respectively.With secondary refining proceeding,average total oxygen content and inclusion amount decrease,the type of most inclusions changes from Al2O3 after tapping to Al2O3-MgO after top slag is formed during ladle furnace refining and finally to CaO-Al2O3-MgO after RH treatment.In the final products,average total oxygen content was 12.7×10-6 and most inclusions were in spherical shape with size less than 5 μm.
参考文献
| [1] | WANG Xin hua;CHEN Bin.Formation of Non-Metallic Inclu sions With Lower Melting Temperatures by Slag-Metal Reaction for High Strength Alloying Steels[A].Gifu:The Iron and Steel Institute of Japan,2008:21. |
| [2] | Abe Takayukil;Furuya Yoshiyukil;Matsuoka Saburo .Significanoe of Size and Type of Inclusions on Giga-Cycle Fatigue in High-Strength Steels[J].Journal of the Iron & Steel Institute of Japan,2003,89(06):711. |
| [3] | JIANG Min;WANG Xin-hua .Formation of MgO @ Al2O3 In clusions in High Strength Alloyed Structural Steel Refined by CaO-SiO2-Al2O3 MgO Slag[J].ISIJ International,2008,48(07):885. |
| [4] | Murakami Y;Kodama S;Konuma S .Quantitative Evaluation of Effects of Non-Metallic Inclusions on Fatigue Strength of High Strength Steels,I:Basic Fatigue Mechanism and Evaluation of Correlation Between the Fatigue Fracture Stress and the Size and Location of Non-Metallic Inclusions[J].International Journal of Fatigue,1989,11:291. |
| [5] | Wang Q Y;Bathias C;Kawagoishi N et al.Effect of Inclusion on Subsurface Crack Initiation and Giga-Cycle Fatigue Strength[J].International Journal of Fatigue,2002,24:1269. |
| [6] | ZHANG Li-feng.Clean Steel and Inclusions[A].Kunming:Metallurgical Industry Press,2004:36. |
| [7] | Tardy P;Karoly Gy.Development of Clean Steel From 1970 to 2002[A].,2002:49. |
| [8] | C. Bertrand;J. Molinero;S. Landa .Metallurgy of plastic inclusions to improve fatigue life of engineering steels[J].Ironmaking & Steelmaking: Products and applications,2003(2):165-169. |
| [9] | 缪新德,于春梅,石超民,杜建峰,朱惠刚,成国光.轴承钢中钙铝酸盐夹杂物的形成及控制[J].北京科技大学学报,2007(08):771-775. |
| [10] | 金利玲,王海涛,许中波,王福明.帘线钢CaO-SiO2-Al2O3-MnO系夹杂物的成分控制[J].北京科技大学学报,2007(04):377-381. |
| [11] | Choudhary S K;Chandra S;Ghosh A .Prediction of Deoxida tion and Inclusion Precipitation in Semi-Killed Steel[J].Metallurgical and Materials Transactions,2005,36B:59. |
| [12] | Hideaki SUITO;Ryo INOUE .Thermodynamics on Control of Inclusions Composition in Ultraclean Steels[J].ISIJ International,1996(5):528-536. |
| [13] | Hiroki OHTA;Hideaki SUITO .Activities in CaO-MgO-Al_2O_3 Slags and Deoxidation Equilibria of Al, Mg, and Ca[J].ISIJ International,1996(8):983-990. |
| [14] | Sakai H.;Suito H. .Liquid Phase Boundaries at 1873 K in the Ternary CaO-Al_2O_3 MO_x(MO_x: MgO, ZrO_2) and CaO-SiO_2-MO_x(MO_x: TiO_2, MgO, Al_2O_3) Systems[J].ISIJ International,1996(2):138-142. |
| [15] | YE Guo-zhu;JONSS Par .Thermodynamics and Kinetics of the Modification of Al2O3 Inclusions[J].ISIJ International,1996,36(Supplement):105. |
| [16] | Korousic B .Fundamental Thermodynamic Aspects of the CaO-Al2O3-SiO2 System[J].Steel Researeh International,1991,62(07):285. |
| [17] | Joo Hyun PARK .Formation Mechanism of Spinel-Type Inclusions in High-Alloyed Stainless Steel Melts[J].Metallurgical and Materials Transactions,2007,38B:657. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%