主要对航天用硅橡胶制品的贮存试验研究进展情况进行了梳理总结,在此基础上指出目前存在以下三方面不足:自然贮存试验开展得少而且数据没有充分挖掘、利用；单应力加速老化试验开展得多,综合应力加速试验开展得少；贮存试验中对产品宏观性能变化关注得多,对其微观结构变化和老化机理研究得少.针对这些问题,指出了今后应在自然贮存试验信息的积累和应用、综合应力贮存试验和贮存老化机理等方面加强研究.
参考文献
| [1] | Zhang L.;He SY.;Xu Z.;Wei Q. .Damage effects and mechanisms of proton irradiation on methyl silicone rubber[J].Materials Chemistry and Physics,2004(2/3):255-259. |
| [2] | Chengmin Wang;Lixin Zhang;Shiyu He;Qiang Wei .Synergistic Effect of Protons and Electrons on Radiation Damage of Silicone Rubber[J].Journal of spacecraft and rockets,2006(3):520-522. |
| [3] | 许妃娟,邱祖民.国内外特种硅橡胶材料的研究进展[J].弹性体,2009(03):60-64. |
| [4] | 邸明伟,张丽新,何世禹,杨德庄.室温硫化硅橡胶及其在航天器上的应用[J].宇航材料工艺,2005(04):7-11,24. |
| [5] | 李昂 .橡胶的老化与寿命估算(续)-第九章橡胶的老化试验及老化变质程度的测定[J].橡胶参考资料,2009,39(04):2-28. |
| [6] | ISO 11346-2004.Rubber,vulcanized or thermoplastic estimation of life-time and maximum temperature of use[S]. |
| [7] | ASTM D 573-2004 (2010).Standard test method for rubber deterioration in an air oven[S]. |
| [8] | TOCT 9.707-1981.聚合物材料气候老化的快速试验方法[S]. |
| [9] | GB/Tr 20028-2005.硫化橡胶或热塑性橡胶应用阿累尼乌斯图推算寿命和最高使用温度[S]. |
| [10] | GB/T 3512-2001.硫化橡胶或热塑性橡胶热空气加速老化和耐热试验[S]. |
| [11] | GJB 92.1-1986.热空气老化法测定硫化橡胶贮存性能导则第一部分-试验规程[S]. |
| [12] | GJB92.2-1986.热空气老化法测定硫化橡胶贮存性能导则第二部分-统计方法[S]. |
| [13] | QJ/Z 164.1-1986.高分子材料热老化试验方法-老化试验导则[S]. |
| [14] | QJ/Z 164.2-1986.高分子材料热老化试验方法-数据处理规范[S]. |
| [15] | ASTM D 3 137-1981(2007).Standard test method for rubber property-hydrolytic stability[S]. |
| [16] | GB/T 15905-1995.硫化橡胶湿热老化试验方法[S]. |
| [17] | Kenneth T. Gillen;Mathew Celina;Robert Bernstein .Validation of improved methods for predicting long-term elastomeric seal lifetimes from compression stress-relaxation and oxygen consumption techniques[J].Polymer Degradation and Stability,2003(1):25-35. |
| [18] | Gillen, KT;Bernstein, R;Derzon, DK .Evidence of non-Arrhenius behaviour from laboratory aging and 24-year field aging of polychloroprene rubber materials[J].Polymer Degradation and Stability,2005(1):57-67. |
| [19] | 解红雨,吴勋,刘春梅,王鑫,张庆雅.硅橡胶密封件随弹贮存老化分析及寿命预估[J].装备环境工程,2011(06):15-18. |
| [20] | Bernstein, R;Gillen, KT .Predicting the lifetime of fluorosilicone o-rings[J].Polymer Degradation and Stability,2009(12):2107-2113. |
| [21] | 张法源.16种实用配方硫化胶长期室内自然老化压缩永久变形变化及预测[J].特种橡胶制品,2002(03):46-49,第4期. |
| [22] | 张法源.16种实用配方硫化胶长期室内自然老化压缩永久变形变化及预测[J].特种橡胶制品,2002(04):56-60,52. |
| [23] | 张发源.3种丁腈橡胶硫化胶加速老化与室内自然老化压缩应力松弛变化[J].特种橡胶制品,2001(02):34-39. |
| [24] | Patel M;Morrell PR;Evans J .Load bearing property testing of a silica filled room temperature vulcanised polysiloxane rubber[J].Polymer Testing,2004(5):605-611. |
| [25] | 颜熹琳,周阳,温茂萍,李敬明,周筱雨,王培.多因素加速老化对硅橡胶泡沫材料力学性能的影响研究[J].化工新型材料,2009(05):66-68. |
| [26] | 周漪,周堃,马宏艳,王莞,何建新.某弹用硅橡胶密封材料贮存寿命预测[J].装备环境工程,2010(05):65-68,83. |
| [27] | 林总君,高劼,王丕毅.不同温、湿度条件下硅橡胶密封圈贮存寿命研究[J].海军航空工程学院学报,2009(02):237-240. |
| [28] | Coons JE;McKay MD;Hamada MS .A Bayesian analysis of the compression set and stress-strain behavior in a thermally aged silicone foam[J].Polymer Degradation and Stability,2006(8):1824-1836. |
| [29] | Patel M;Skinner A R .Thermal aging studies on room-temperature vulcanized polysiloxane rubbers[J].Polymer Degradation and Stability,2001,73:399-402. |
| [30] | Patel, M;Morrell, PR;Murphy, JJ .Continuous and intermittent stress relaxation studies on foamed polysiloxane rubber[J].Polymer Degradation and Stability,2005(1):201-206. |
| [31] | 田蓉丽 .HM301硅橡胶使用寿命的评估[J].理化检验-物理分册,2009,45:529-531. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%