以偶氮二异丁腈(AIBN)为引发剂,N-乙烯吡咯烷酮(NVP)单体、甲基丙烯酸-β-羟乙酯(HEMA)单体、γ-(甲基丙烯酰氧)丙基三甲氧基硅烷(KH570)单体及交联剂N,N'-亚甲基双丙烯酰胺(Bis)在一定温度下共聚制得软性角膜接触镜材料--水凝胶,并采用池膜测量法研究了钠离子在角膜接触镜材料中的渗透性能.实验发现,随NVP含量的增大,水凝胶的含水量增大,钠离子渗透性能增强;KH570含量小于15%时,钠离子渗透性能随KH570含量的增加而增强,而含量在15%~25%时钠离子渗透性能则降低;交联剂含量增大会降低钠离子的渗透性能,含量以不超过0.7%为宜.
参考文献
[1] | Peppas N A.Hydrogels in medicine and pharmacy[M].Boca Raton:CRC Press Inc,1986 |
[2] | Franklin V J;Bright A M;Tighe B J .Hydrogel polymers and ocular spoilation process[J].Trends in Polymer Science,1993,1:9. |
[3] | COMPAN V.;LOPEZ M.L.;ANDRIO A.;LOPEZ-ALEMANY A.;REFOJO M.F. .Determination of the Oxygen Transmissibility and Permeability of Hydrogel Contact Lenses[J].Journal of Applied Polymer Science,1999(3):321-327. |
[4] | Compan V;Guzman J;Riande E .A potentiostatic study of oxygen transmissibility and permeability through hydrogel membranes.[J].Biomaterials,1998(23):2139-2145. |
[5] | Griesser H J;Laycock B G .Extended wear ophthalmic lens[P].WO 9631792,1996-10-10. |
[6] | 贾绍义;柴诚敬.化工传质与分离过程[M].北京:化学工业出版社,2001 |
[7] | 韩慧芳 .有机硅改性PVP水凝胶软接触透镜材料的合成与性能研究[D].广东工业大学,2004. |
[8] | 谭帼馨,崔英德.NVP-HEMA角膜接触镜材料的透氧性能[J].膜科学与技术,2004(02):26-29. |
[9] | 黎新明 .共聚物水凝胶接触镜材料的制备与性能研究[D].西北工业大学,2003. |
[10] | 郑荣领,周电根,郑一仁.角膜接触镜研究进展[J].中国实用眼科杂志,2000(05):262-265. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%