为提高无取向电工钢成品性能及优化生产,采用SEM-EDS等分析方法分别对比分析了无取向电工钢生产时,不同酸溶铝含量的生产工艺对钢中夹杂物的影响.研究表明,当钢中酸溶铝含量w(Als)为0.2％～0.4％时,精炼过程所生成的夹杂物为高熔点的Al2O3和球状的MgO-Al2O3类夹杂物；当钢中w(A1s)小于0.005％时,精炼过程所生成的夹杂物主要为塑性硅铝锰酸盐类夹杂；各工位夹杂物平均数量呈递减的趋势,且w(A1s)为0.2％～0.4％的高碱度渣系控制生成的夹杂物总量低于后者.
参考文献
| [1] | 何忠治.硅钢[M].北京:冶金工业出版社,1996:280. |
| [2] | Mimura T.Control of Inclusions in Tire Cord Steel and Valve Spring Steel[A].Nagoya,ISIJ,2005:27. |
| [3] | Kawakami K;Taniguchi T;Nakashima K .Generation Mechanisms of Non-Metallic Inclusions in High-Cleanliness Steel[J].Tetsu To Hagane-Journal of the Iron & Steel Institute of Japan,2007,93:741. |
| [4] | Boc I .Analysis of Inclusions in Cold Rolled Si-Fe Strips[J].Journal of Magnetism and Magnetic Materials,1990,83:381. |
| [5] | Gatellier C;Gaye H .Inclusions Control in Low-Aluminum Steel[J].La Revue de Metallurgie-CIT,1992,89(04):361. |
| [6] | 陈书浩,王新华,何肖飞,姜敏,黄福祥.帘线钢中酸溶铝含量的变化及其对夹杂物的影响[J].钢铁,2011(10):42-47. |
| [7] | 张国兴,王谦,何生平,曾建华.超低碳钢弱脱氧工艺下炉渣组分的控制[J].钢铁,2011(05):38-42. |
| [8] | 蔡开科.转炉冶炼低碳钢终点氧含量控制[J].钢铁,2009(05):27-31. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%