针对纤维增强复合材料层板开孔压缩，将复合材料层板的失效分为层内失效和层间失效，建立了复合材料层板开孔压缩损伤分析模型。该模型基于逐渐损伤分析，对不同复合材料开孔层板进行了失效预测，并与文献中试验结果进行了对比，破坏强度和失效模式均与文献试验结果非常吻合。结果表明，本文中所建立的层板开孔压缩损伤分析模型能够模拟含孔层合板压缩过程中的损伤起始、损伤扩展和最终破坏，并最终预测含孔层合板压缩失效模式和破坏强度。
A model for the damage analysis of the open-hole compression composite laminates was developed. The model divided the failure modes of composite laminates into intra-laminar and inter-laminar damage. The failure modes and failure loads of different laminates were predicted and compared with the experimental results based on progressive failure analysis methodology. The results show that the model can simulate damage initiation, damage progression, final damage and predicted failure mode and failure load of laminates with central circular holes subjected to compression load, then predict the failure mode and failure load of open-hole compression laminates.
参考文献
| [1] | Soutis C. Damage tolerance of open- hole CFRP laminates loaded in compression [J]. Composite Engineering, 1994, 4(3) : 317-327. |
| [2] | Suemasu H, Takahashi H, Ishikawa T. On failure mechanisms of composite laminates with an open hole subjected to compressive load [J]. Composites Science and Technology, 2006, 66: 634-641. |
| [3] | Soutis C, Curtisb P T. A method for predicting the fracture toughness of CFRP laminates failing by fibre microbuekling [J]. Composites: Part A, 2000, 31: 733-740. |
| [4] | Lee J, Soutis C. Measuring the notched compressive strength of composite laminates: Specimen size effects [J]. Composites Science and Technology, 2008, 68: 2359-2366. |
| [5] | Wisnom M R, Hallett S R. Scaling effects in notched composites [J]. Journal of Composite Materials, 2010, 44(2) : 195-210. |
| [6] | 崔海涛,温卫东,郝勇.碳纤维增强复合材料含孔层合板损伤破坏分析研究进展[J].材料导报,2002,16(2):43-45. |
| [7] | 程小全,康圻蒙,等.平面编织复合材料层合板低速冲击后拉伸性能[J].复合材料学报,2008,25(5):163-168. |
| [8] | 崔海坡,温卫东,崔海涛.含孔复合材料层合板在压缩载荷下的三维逐渐损伤[J].机械工程学报,2006,42(8):89-94. |
| [9] | Knight N F J. Factors influencing progressive failure analysis predictions for laminated composite structure [ C ] // Proceedings of the 49th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Materials Conference. Schaumburg, Illinois: AIAA, 2008 |
| [10] | Chang F K, Chang K Y. A progressive damage model for laminated composites containing stress concentrations [J]. Journal of Composite Materials, 1987, 21: 834-855. |
| [11] | Chang F K, Lessard L. Damage tolerance of laminated composites containing an open hole and subjected to tensile loadings [J]. Journal of Composite Materials, 1991, 25: 274- 301. |
| [12] | Tan S. A progressive failure model for composite laminates containing openings [J]. Journal of Composite Materials, 1991, 25: 556-574. |
| [13] | Gama B A, Xiao J, Haque M J, et al. Experimental and numerical investigations on damage and delamination in thick plain weave S - 2 glass composites under quasi static punch shear loading [C]//18th Annual Technical Conference of American Society for Composites. Florida: University of Florida, 2003 |
| [14] | Ambur D R, Jaunky N, Vila C G D. Progressive failure of composites laminates using LaRC02 failure criteria [C] // Proceedings of the 45th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Materials Conference. Palm Springs, California: AIAA, 2004 |
| [15] | Camanho P P, Maiml P, Ddvila C G. Prediction of size effects in notched laminates using continuum damage mechanics [J].Composite Science and Technology, 2007, 67: 2715-2727. |
| [16] | Lapczyk I, Hurtado J A. Progressive damage modeling in fiber-reinforced materials[J]. Composites: Part A, 2007, 38: 2333-2341. |
| [17] | Lorriott T, Marion G, Harry R, et al. Onset of free- edge delamination in composite laminates under tensile loading [J]. Composites Part B: Engineering, 2003, 34: 459-471. |
| [18] | Yang Q, Cox B. Cohesive models for damage evolution in laminated composites [J]. International Journal of Fracture, 2005, 133(2): 107-137. |
| [19] | Hashin Z, Rotem, A. A fatigue failure criterion for fiber- reinforced composite materials [J]. Journal of Composite Materials, 1973, 7: 448-464. |
| [20] | Anon. ABAQUS user's manual [CP]. Version 6.10. Pawtucket: Hibbitt, Karlsson and Sorensen, 2010 |
| [21] | Turon A, Davila C G, Camanho P P, et al. An engineering solution for mesh size effects in the simulation of delamination using cohesive zone models [J]. Engineering Fracture Mechanics, 2007, 74(10): 1665-1682. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%