以硝酸钡、硝酸锶,钛酸四丁脂以及氨水为原料,利用柠檬酸-硝酸盐燃烧法制备了Ba0.5Sr0.5TiO3(BST)超细粉末。详细研究了pH值、分散剂对形成BST粉末粒度的影响.用所合成的粉末压片,1300℃烧结2h即可获得致密烧结体,烧结样品的平均粒径约为1μm.在10kHz,25℃下的介电性能为:介电常数1470,介电损耗0.006。
Ultra-fine Ba0.5Sr0.5TiO3 (BST) powder was prepared by using barium nitrate, strontium nitrate, tetra-n-butyl titanate, and ammonium hydroxide
via citrate-nitrate combustion process. The pH value and dispersant, strongly influencing on the particle distribution of BST
powder, were investigated in detail. The precursor powders were pressed into tablets(φ=20.0mm, d=5.0 mm)and then fully sintered at
1300℃ for 2h.At 25℃, the dielectric constant and dissipation factor of the sintered sample were 1470 and 0.006 at 10kHz,
respectively, measured by a HP4192A Impedance.
参考文献
| [1] | Ezhilvalavan S, et al. Mater. Chemistry and Physics, 2000, 65: 227--248. [2] PANDA B, et al. J. MATER SCI: MATER. ELECTRONICS, 2002, 13: 263--268. [3] YOON Ki Hyun, et al. J. Appl Phys., 2001, 40 (9B): 5497--5500. [4] Chang H, et al. Appl. Phys. Lett., 1999, 74 (8): 1165--1167. [5] Annual report of Tanka kikinsoku, Japan. [6] Hwang C S. Mater. Sci. and Engineering, 1998, (B56): 178--190. [7] Liu S B, et al. Mater. Sci. Engineering C, 2002, (22): 73--77. [8] Noda M, et al. Sensors and Actuators, 1999, 77: 39--44. [9] Zhu W, et al. J. Appl. Phys., 1998, 84 (9): 5134--5139. [10] Zhu W, et al. J. Mater. Res., 2000, 15 (6): 1291--1302. [11] Chang H, et al. Appl. Phys. Lett., 1999, 74 (8): 1165--1167. [12] KAKIHANA M. Journal of Sol-Gel Science and Technology, 1996, 6: 7--55. [13] 李承恩, 等(LI Cheng-En, et al). 无机材料学报(Journal of Inorganic Materials), 1982, 10 (1): 9--16. [14] Majumder S B, et al. J. Appl. Phys., 2001, 90 (2): 896--903. [15] 曾华荣, 等(ZENG Hua-Rong, et al), 无机材料学报(Journal of Inorganic Materials), 1999, 14 (1): 101--106. [16] Cole M W, et al. J. Appl. Phys., 2002, 92 (1): 475--483. [17] Lee S Y, Tseng T Y. Appl. Phys. Lett., 2002, 80 (10): 1797--1799. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%