采用高能球磨和晶化热处理方法制备钕铁吸波粉体,研究Si含量对钕铁粉体吸波性能的影响.结果发现:在高能球磨和微氧化气氛下进行700℃,1h晶化处理后,Nd8Fe92、Nd8Fe89Si3和Nd8Fe87S5粉体组织均由α-Fe、Nd2O3和Fe17Nd2相组成,加入Si后,粉体的Fe17Nd2相对量增加；Nd8Fe92粉体的反射率最小值约为-4.5 dB,吸收峰频率约为4.4 GHz,加入Si后,粉体的反射率最小值降低,吸收峰频率升高,吸波带宽变宽；Nd8Fe92粉体以介电损耗为主,Nd8Fe89Si3和Nd8Fe87Si5粉体以磁损耗为主.
参考文献
| [1] | 邱琴,张晏清,张雄.电磁吸波材料研究进展[J].电子元件与材料,2009(08):78-81. |
| [2] | Liu Junhu;Ma Tianyu;Tong Hui et al.[J].J ournal ofMagnet ism and Magnetic Materials,2010,322(08):940. |
| [3] | Xie Guozhi;Wang Ping;Zhang Baoshan et al.[J].J ournal ofMagnet ism and Magnetic Materials,2008,320(06):1026. |
| [4] | Lima UR;Nasar MC;Nasar RS;Rezende MC;Araujo JH .Ni-Zn nanoferrite for radar-absorbing material[J].Journal of Magnetism and Magnetic Materials,2008(10):1666-1670. |
| [5] | Keefer's Rees;Lazareva;Lavalle Husband.微波吸收材料[M].北京:科学出版社,1986:50. |
| [6] | 周寿增.超强永磁体:稀土铁系永磁材料[M].北京:冶金工业出版社,2004:165. |
| [7] | 许传才.铁合金冶炼工艺学[M].Xi'an:Northwestern University Press,1991:59. |
| [8] | 日本钢铁协会.新版钢铁技术讲座第3卷:钢材的性能与试验[M].上海:上海科学技术出版社,1981:211. |
| [9] | 吕瑞涛,康飞宇,韦进全,顾家琳,王昆林,吴德海.填充α-Fe碳纳米管的电磁性能研究[J].无机材料学报,2008(01):23-28. |
| [10] | 廖绍彬.铁磁学[M].北京:科学出版社,1988:41. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%