通过对深冷及钝化处理工艺下W6Mo5Cr4V2高速钢磨损情况的研究,以及对其微观组织进行SEM观察和磨痕分析,分析了磨损机理以及耐磨性提高的原因.结果表明:未深冷试样以粘着磨损为主,深冷以及钝化处理后的试样以氧化磨损为主;深冷处理可以显著提高材料的硬度和耐磨性,相比于深冷处理前耐磨性可以提高1.5倍,这是由于深冷处理后析出碳化物的平均尺寸减小为深冷处理前的一半左右,碳化物数目约增长了46%,而且分布更加均匀;钝化处理工艺不改变材料的硬度,但是可以改善材料初期的磨损情况,减小振动,提高耐磨性,这是由于钝化处理工艺促进材料表层出现含碳的薄膜,有一定润滑作用,从而改善了材料的耐磨性.

参考文献

[1] 韩晓君;李淑娟;闫献国;王旭强.深冷处理对高速钢磨削表面残余应力的影响[J].热加工工艺,2015(2):227-231.
[2] D. Das;A.K. Dutta;K.K. Ray.Optimization of the duration of cryogenic processing to maximize wear resistance of AISI D2 steel[J].Cryogenics,20095(5):176-184.
[3] Simranpreet Singh Gill;Jagdev Singh;Rupinder Singh;Harpreet Singh.Effect of Cryogenic Treatment on AISI M2 High Speed Steel: Metallurgical and Mechanical Characterization[J].Journal of Materials Engineering and Performance,20127(7):1320-1326.
[4] 段春争;王敏杰.高速钢循环深冷处理后的显微组织和力学性能[J].金属热处理,2008(3):90-93.
[5] 闫献国;庞思勤;李永堂.高速钢深冷处理技术研究进展[J].新技术新工艺,2008(3):14-18.
[6] 桂育鹏.刀具刃口钝化技术的探讨[J].数控机床市场,2005(12):96-100.
[7] X. G. Yan;D. Y. Li.Effects of the sub-zero treatment condition on microstructure, mechanical behavior and wear resistance of W9Mo3Cr4V high speed steel[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20131/2(1/2):854-862.
[8] Flavio J. da Silva;Sinesio D. Franco;Alisson R. Machado;Emmanuel O. Ezugwu;Antonio M. Souza Jr..Performance of cryogenically treated HSS tools[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20065/6(5/6):674-685.
[9] 彭菲;郭宏;闫献国;李俊吉.丝锥全生命周期参数对攻丝性能影响的研究[J].制造技术与机床,2015(4):88-91.
[10] N. B. Dhokey;J. V. Dandawate.Study of Wear Stabilisation in Cryoprocessed Cobalt-Based High Speed Steel[J].Transactions of the Indian Institute of Metals,20124(4):405-412.
[11] D. Das;A. K. Dutta;K. K. Ray.Inconsistent wear behaviour of cryotreated tool steels: role of mode and mechanism[J].Materials Science and Technology,200910(10):1249-1257.
[12] D. Das;K. K. Ray;A. K. Dutta.Influence of temperature of sub-zero treatments on the wear behaviour of die steel[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20099/10(9/10):1361-1370.
[13] D. DAS;A. K. DUTTA;V. TOPPO.Effect of Deep Cryogenic Treatment on the Carbide Precipitation and Tribological Behavior of D2 Steel[J].Materials and Manufacturing Processes,20073/4(3/4):474-480.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%