为了探究激光冲击强化对SiCp/Cu复合材料力学性能的影响,采用有限元分析软件ANSYS/LS-DYNA对复合材料单胞模型进行冲击加载,模拟结果显示:在基体金属上存在着广泛的压应力,并且在载荷作用过程中导致了基体的屈服强化,大大提高了基体的强度;在基体与颗粒增强体之间的界面上存在着一定的等效应力值.采用WDW-200微机控制式电子万能试验机对激光冲击强化前后的试样进行拉伸性能对比试验:发现冲击后试样的抗拉强度较未冲击试样的提高了18 MPa,且断口呈现韧窝形貌,为微孔聚集形韧性断裂.结果表明:激光冲击强化提高了SiCp/Cu复合材料的力学性能.
参考文献
| [1] | 董任节;史耀武.[J].Foreign Metal Heat Treatment (国外金属热处理),1999(06):9. |
| [2] | Fairand B P;Wilcox B A;Gallaghtr W J et al.[J].Journal of Applied Physics,1972,43(09):3893. |
| [3] | Fairand B P;Claur A H .[J].Industrial Applications of High Power Laser Technology,1976,86:112. |
| [4] | Fairand B P;Clauer A H.[J].Journal of Applied Physics,1979:50. |
| [5] | Fabbro R;Fournier J;Ballard P et al.[J].Journal of Applied Physics,1990,68(02):46. |
| [6] | Jean-Eric Masse;Gerard Barreau .[J].Surface and Coatings Technology,1995,70:231. |
| [7] | Peyre P;Fabbro R .[J].Optical and Quantum Electronics,1995,27:1213. |
| [8] | Peyre P;Fabbro R;Berthe L et al.[J].Journal of Laser Appli-cation,1996,8:135. |
| [9] | Peyre P;Fabbro R;Merrian P et al.[J].Materials Science and Engineering,1996,A210:102. |
| [10] | Chu J P;Rigsbee J M;Babas G et al.[J].Materials Science and Engineering,1999,A260:260. |
| [11] | 胡永祥;姚振强;胡俊 .[J].China Laser(中国激光),2006,33(06):846. |
| [12] | Bao G;hutchinson J W;McMeeking R M .[J].Acta Metallurgica Et Materialia,1991,39:1871. |
| [13] | 邵军超;刘越 .[J].Material Review(材料导报),2007,21(09):111. |
| [14] | Peyre P;Fabbro R;Merrien P et al.[J].Materials Science and Engineering,1996,A210:102. |
| [15] | 张永康;周建忠;叶云霞.Laser Processing Technology(激光加工技术)[M].北京:化学工业出版社,2004:259. |
| [16] | 吴晶;李文芳;蒙继龙 .[J].Journal of Materials Science and Engineering(材料科学与工程学报),2003,21(01):21. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%