为了解Co元素对新型奥氏体不锈钢抗硫酸钠熔盐热腐蚀性能的影响,采用X射线衍射仪(XRD)和扫描电子显微镜(SEM)等研究了含Co元素的新型奥氏体不锈钢热腐蚀层的物相组成和微观形貌,获得了不同Co含量的新型奥氏体不锈钢的腐蚀失重速率,并讨论了Co元素对该不锈钢腐蚀层以及耐热腐蚀性的影响.结果表明:在该不锈钢中添加Co元素能够一定程度上改善和提高其抗硫酸钠熔盐热腐蚀性能;Co有利于增强氧化膜的黏附性和致密性,推迟氧化膜的破裂时间,延长热腐蚀孕育期;Co也能有效延缓S元素在不锈钢基体中的扩散,减缓硫化-氧化速率,从而改善和提高合金的抗热腐蚀性能.
参考文献
| [1] | Yamamoto Y;Brady MP;Lu ZP;Maziasz PJ;Liu CT;Pint BA;More KL;Meyer HM;Payzant EA.Creep-resistant, Al2O3-forming austenitic stainless steels.[J].Science,20075823(5823):433-436. |
| [2] | M.P. Brack;V. Yamamoto;M.L. Sanlella.The Development of Alumina-Forming Austenitic Stainless Steels for High-Temperature Structural Use[J].JOM,20087(7):12-18. |
| [3] | M.P. Brady;Y. Yamamoto;B.A. Pint.On the Loss of Protective Scale Formation in Creep-Resistant, Alumina-Forming Austenitic Stainless Steels at 900 deg C in Air[J].Materials Science Forum,2008Pt.2(Pt.2):725-732. |
| [4] | Y.F. Yan;X.Q. Xu;D.Q. Zhou;H. Wang;Y. Wu;X.J. Liu;Z.P. Lu.Hot corrosion behaviour and its mechanism of a new alumina-forming austenitic stainless steel in molten sodium sulphate[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2013Dec.(Dec.):202-209. |
| [5] | 付广艳;李剑光;刘群.涂敷Na2SO4盐膜的Ni基合金在900℃空气中的热腐蚀[J].沈阳化工大学学报,2013(4):353-357. |
| [6] | 卢旭东;陈涛;李光瑞.一种镍基合金850℃的盐膜热腐蚀行为[J].电镀与精饰,2013(5):36-38,46. |
| [7] | 王健;李辰昊;张铁邦;李金山;张平祥.Ni-Cr-W基高温合金熔盐环境中的热腐蚀行为[J].宇航材料工艺,2014(6):26-29. |
| [8] | 卢旭东;田素贵;陈涛;郭策安;李光瑞.高铬镍基合金熔融硫酸盐热腐蚀过程中内氧化和内硫化行为的研究[J].稀有金属材料与工程,2014(1):79-84. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%