为了实现C/SiC复合材料与难熔金属的连接,通过熔盐法在C/SiC复合材料表面沉积钛金属层.用SEM和EDS研究金属化层的形貌及成分;用X射线衍射分析金属化层的相组织:用定量金相法测量钎焊料的铺展特性.研究表明:钛金属化层均匀致密,与基体结合紧密,钛金属可渗入纤维间孔隙,比较完整地包覆在C/SiC复合材料外表面.金属化层主要成分为TiC、Ti5Si3.金属化层与SiC界面分为3层,由内到外主要成分为Ti5Si3、TiC和Ti5Si3.表面金属化后的C/SiC复合材料与钛合金钎焊料润湿性明显改善,润湿角从153.9°降低为13.2°.
Ti metallized coating was prepared on the surface of carbon fiber reinforced silicon carbide matrix (Cf/SiC) composite by molten salt reaction to make joining the composite with high melt point metals such as Ti. The morphologies and compositions of Ti metallized coating were analyzed by SEM and EDS. The phase components were assessed by XRD. The wettability of the solder was measured by quantitative metallography. The results show that Ti metallized coating is uniform and dense, and bound with the matrix closely. Ti can infiltrate into the gaps of the fibers, and cover the surfaces of the Cf/SiC composite. The main phases of the metalized coating consist of TiC and Ti5Si3. There are three transition layers between SiC and the metallized, I. E. Ti5Si3 layer, TiC layer and Ti5Si3 layer. The wettability of Cf/SiC composites surface to Ti is greatly improved by metallization, and the contact angle is deceased from 153.9° to 13.2° at 950 ℃.
参考文献
| [1] | Naslain R et al.[J].Composites Science and Technology,2004,64(02):155. |
| [2] | 黄奇良,潘伟,胡忠.利用热歧化反应进行氮化铝陶瓷表面钛金属化工艺及正交实验研究[J].现代技术陶瓷,2001(04):3-6,15. |
| [3] | 李建强,潘伟,陈健,房明浩,潘紫霄.利用熔盐热析出反应法对AlN陶瓷表面金属化研究[J].无机材料学报,2003(05):1086-1090. |
| [4] | 黄奇良,潘伟,胡忠.氮化铝陶瓷表面钛金属化的研究[J].材料导报,2002(02):66-68. |
| [5] | 黄奇良,潘伟,张直.AlN陶瓷表面钛金属化沉积的动力学研究[J].硅酸盐通报,2004(01):8-12. |
| [6] | 王松,陈朝辉,索相波,郑文伟.T300碳纤维热处理对Cf/SiC复合材料性能的影响[J].材料工程,2004(12):40-42,46. |
| [7] | Yang Y Q et al.[J].Composites Part A:Applied Science and Manufacturing,1998,29(1-2):1235. |
| [8] | Labis J.;Hirai M.;Kusaka M.;Iwami M.;Ohi A. .Interfacial reaction study of thermally annealed Ti film on 4H-SiC by soft X-ray emission spectroscopy[J].Surface Science: A Journal Devoted to the Physics and Chemistry of Interfaces,2001(1/3):447-452. |
| [9] | Fromentin J F et al.[J].Composites Science and Technology,1996,56(07):767. |
| [10] | Duda C et al.[J].Composites Part A:Applied Science and Manufacturing,2004,35(05):511. |
| [11] | 张祖力,王华,鞠华,罗松,陈小军.陶瓷与金属密封技术的研究[J].功能材料,2006(02):312-314. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%