以甲基丙烯酸甲酯(MMA)、醋酸乙烯酯(VAc)和丙烯酸锂(LiAA)为单体,采用种子乳液聚合法制备了(P(MMA-VAc-LiAA)三元共聚物.利用红外光谱(FTIR),核磁共振(~1HNMR),差示扫描量热(DSC) /热重分析(TG),X射线衍射(XRD),扫描电镜(SEM)等方法对聚合物的结构进行了表征.将P(MMA-VAc-LiAA)与LiClO_4共混,采用流延法制备了聚合物电解质膜,用交流阻抗方法测试了电解质膜的电导率,结果表明,该聚合物电解质室温离子电导率可以达到10~(-3)S/cm.而且离子电导率随着温度的升高而迅速增加,电导率-温度曲线符合Arrhenius方程.机械性能测试结果表明,在P(MMA-VAc)的基础上,引入第三单体LiAA可以改善膜的收缩性与力学性能.
The ternary copolymer polymethyl methacrylate-vinyl acetate-lithiumacrylate P(MMA-VAc-LiAA)was synthesized by seeded radical emulsion polymerization, with methyl methacrylate (MMA), vinyl acetate (VAc) and lithiumacrylate (LiAA) as monomers.The performances of the polymer were characterized by FTIR, XRD, DSC/TG, and SEM.The polymer electrolytes was prepared by blending P(MMA-VAc-LiAA)and LiClO_4 with solution casting technique.The ionic conductivity of the electrolyte membrane was tested by AC impedance, which demonstrated that the ionic conductivity of polymer electrolytes was as high as 10~(-3)S/cm at room temperature.And the ionic conductivity increased with increasing temperature, the conductivity-temperature plots were found to follow an Arrhenius nature.The introduction of the third monomer LiAA to P(MMA-VAc) improved the contraction and mechanical properties of membrane, which meeted the existing requirements of lithium-ion battery.
参考文献
| [1] | Chiu CY;Yen YJ;Kuo SW;Chen HW;Chang FC .Complicated phase behavior and ionic conductivities of PVP-co-PMMA-based polymer electrolytes[J].Polymer: The International Journal for the Science and Technology of Polymers,2007(5):1329-1342. |
| [2] | Fenton D M;Parker J M;Wright P V .[J].Polymer,1973,14:589-592. |
| [3] | Manuel Stephan A .[J].European Polymer Journal,2006,42:21-42. |
| [4] | Baskaran R;Selvasekarapandian S;Kuwata N et al.[J].Solid State Ionics,2006,177:26-32. |
| [5] | Gao Kun;Hu Xinguo;Yi Tingfeng et al.[J].Electrochimica Acta,2006,52:443-449. |
| [6] | Zhoua D Y;Wanga G Z;Li W S et al.[J].Journal of Power Sources,2008,184:477-480. |
| [7] | 杨道均,傅相锴,龚永锋.P（VAc-MMA）为基体的聚合物电解质研究[J].化学学报,2008(08):975-979. |
| [8] | Lee K H;Park J K;Kim W J .[J].Electrochimica Acta,2000,45:1301-1306. |
| [9] | Zhang Lan;Zhang Shichao .[J].Electrochimica Acta,2008,54:606-610. |
| [10] | Gomez, ED;Panday, A;Feng, EH;Chen, V;Stone, GM;Minor, AM;Kisielowski, C;Downing, KH;Borodin, O;Smith, GD;Balsara, NP .Effect of Ion Distribution on Conductivity of Block Copolymer Electrolytes[J].Nano letters,2009(3):1212-1216. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%