利用自行研制的管流动态模拟试验装置,研究了碳钢在液/固双相流中的磨损腐蚀。结果表明:碳钢在含有5%河砂的双相流动3.5%NaCl溶液中,磨损腐蚀速度随流速的增加而显著增大,没有像单相流中出现磨损腐蚀速度显著降低的流速区段,其磨损腐蚀过程仍主要受阴极氧扩散控制。对碳钢施加阴极电流,由于抑制了腐蚀电化学因素,从而大幅度削弱了与流体力学因素间的协同效应,使碳钢的磨损腐蚀大大减轻。
The electrochemical behavior in erosion-corrosion of carbon steel in flowing liquid-solid double phase solution was studied with self-made flow loop simulating apparatus. The experimental results showed that erosion-corrosion rate in flowing double phase 3.5% NaCl solution containing 5% sand increases markedly with increasing flow velocity. But it was not found that the erosion-corrosion rate-decreased region which happened in flowing single phase solution existed. The erosion-corrosion process of carbon steel in flowing liquid-solid double phase solution is still controlled by cathodic oxygen diffusion process. Once cathodic current was impressed on carbon steel, the erosion-corrosion rate of carbon steel decreases abruptly because the corrosion electrochemistry factor is restrained and the synergism is weakened. It was verified that corrosion electrochemical factor plays a dominant role in erosion-corrosion.
参考文献
[1] |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%