采用固相反应法制备出了(Bi_(1.975) Li_(0.025))(Zn_(2/3) Nb_(4/3-x) V_x)O_7陶瓷,研究了锂、钒掺杂对于Bi_2(Zn_(1/2) Mb_(2/3))_2 O_7(BZN)陶瓷烧结温度、相结构和介电性能的影响.结果表明:锂、钒掺杂能显著降低BZN陶瓷的烧结温度,可由1 000℃降至860℃;当掺杂量x≤0.05时,陶瓷相结构保持单一的单斜焦绿石相,介电损耗出现明显的弛豫现象;当x为0.005,0.01,0.02和0.05时,陶瓷的介电弛豫峰值温度分别为125,120,112,100℃,介电弛豫激活能的减小使弛豫温区向低温方向移动.
(Bi_(1.975) Li_(0.025))(Zn_(2/3) Nb_(4/3-x) V_x)O_7 (BLZNV) ceramics were prepared by solid phase reaction.The effect of (Li,V) dope on sintering temperature,phase structure and dielectric properties of Bi_2 (Zn_(1/3) Nb_(2/3))_2 O_7 (BZN) ceramics was investigated.The results show that (Li,V) doping could decrease the sintering temperature of the BZN ceramic remarkably from 1 000 ℃ to 860 ℃.The ceramics had single monoclinal pyrochlore phase when x≤0.05.Relaxation appeared during dielectric loss.When x were 0.005,0.01,0.02 and 0.05,the peak temperatures of (Li,V) doped samples were 125,120,112 and 100 ℃,respectively.A shift of the relaxation peak to low temperature was caused by activation energy decreasing.
参考文献
[1] | Shen B;Zhai JW;Yao X .Dielectric relaxation and tunability of Bi2O3-ZnO-CaO-Ta2O5 ceramics[J].Applied physics letters,2005(7):2902-1-2902-3-0. |
[2] | 沈波,刘艳平,姚熹.(Bi2-yCay)(Zn1/3 Ta2/3)2O7陶瓷的介电弛豫和介电性能[J].硅酸盐学报,2006(02):237-242. |
[3] | Valant M.;Davies P.K. .Crystal Chemistry and Dielectric Properties of Chemically Substituted (Bi_(1.5)Zn_(1.0)Nb_(1.5))O_7 and Bi_2(Zn_(2/3)Nb_(4/3))O_7 Pyrochlores[J].Journal of the American Ceramic Society,2000(1):147-153. |
[4] | Nino JC.;Randall CA.;Lanagan MT. .Dielectric relaxation in Bi2O3-ZnO-Nb2O5 cubic pyrochlore[J].Journal of Applied Physics,2001(8):4512-4516. |
[5] | 周焕福,黄金亮,王茹玉,殷镖,孙道明.BiVO4掺杂对(Bi1.5Zn0.5)(Zn0.5Nb1.5)O7陶瓷介电性能的影响[J].硅酸盐学报,2005(12):1453-1456. |
[6] | Dielectric properties of Bi_(2)O_(3)-ZnO-Ta_(2)O_(5) pyrochlore and zirconolite structure ceramics[J].Applied physics letters,2003(21):3734-3736. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%