采用助熔剂自发成核法,以Li2CO3-2MoO3为助熔剂,生长出了Yb∶ NdPO4晶体.通过X射线粉末衍射和X射线能谱技术对所得的晶体进行了表征.结果表明,少量Yb3+掺入到了NdPO4晶体中,但并未改变NdPO4晶体的晶格结构.比较了Yb∶ NdPO4晶体和NdPO4晶体室温下的透过光谱.测量了室温下晶体的荧光光谱,泵浦光波长为332 nm.结果表明晶体的最强荧光发射峰位于995nm,归属于Yb3+从激发态2F5/2到基态2F7/2的电子跃迁.1059nm的发射峰归属于Nd3+从4 F3/2到4I11/2的电子跃迁.Nd3+的发射峰强度较弱,表明在室温下晶体中主要发生了Nd3+ →Yb3的能量传递.

参考文献

[1] Hong H Y P;Dwight K .Crystal Structure and Fluorescence Lifetime of NdAl3 (BO3) 4,a Promising Laser Material[J].Materials Research Bulletin,1974,9(12):1661-1665.
[2] Lutz F;Leiss M;Müller J .Epitaxy of NdAl3(BO3)4 for Thin Film Miniature Lasers[J].Journal of Crystal Growth,1979,47(01):130-132.
[3] 王继扬,姚淑华,黄林勇.四硼酸铝钕晶体及其小型全固态激光器[J].物理学进展,2010(01):81-99.
[4] Albrand K R;Attig R;Fenner J et al.Crystal Structure of the Laser Material NdP5O14[J].Materials Research Bulletin,1974,9:129-140.
[5] Danielmeyer H G;Jeser J P;Sch(o)nherr E et al.The Growth of Laser Quality NdP5 O14 Crystals[J].Journal of Crystal Growth,1974,22(04):298-302.
[6] Hong H YP;Chinn S R .Influence of Local-sit e Symmetry on Fluorescence Lifetime in High-Nd-concentration Laser Materials[J].Materials Research Bulletin,1976,11(05):461-468.
[7] John B. Gruber;Dhiraj K. Sardar;Toomas H. Allik;Bahram Zandi .Spectra and energy levels of Nd~(3+) (4f~3) in stoichiometric NdP_5O_(14)[J].Optical materials,2004(2):351-358.
[8] Yongzheng Wang;Jing Li;Jiyang Wang;Shujuan Han;Yongjie Guo .Flux growth and characterizations of NdPO_4 single crystals[J].Journal of Crystal Growth,2010(19):2779-2782.
[9] Robinson M;Asawa C K .Stimulated Emission from Nd3 + and Yb3 + in Noncubic Sites of Neodymium and Ytterbium-doped CaF2[J].Journal of Applied Physics,1967,38:4495-4501.
[10] 陈述春,茅森,戴凤妹.磷酸盐玻璃中Yb3+和Nd3+之间的声子参助能量转移[J].物理学报,1984(04):515-522.
[11] 金晶,夏海瑞,孙尚倩,冉栋刚,刘凤芹,毕文婕,张怀金,程艳.Nd:YbVO4晶体的拉曼光谱和荧光光谱研究[J].人工晶体学报,2008(06):1330-1336.
[12] Znamierowska T;Bandrowski S .Investigation of Phase Equilibria in the System Nd2O3-Na2O3-P2O5[J].Solid State Sciences,2008,10:1671-1677.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%