研究了热压/热变形纳米复合永磁体制备的新工艺,探讨了制备高性能高各向异性块状纳米复合永磁体的新方法.以晶态纳米复合永磁粉末为原料,研究了热压/热变形工艺参数与磁体密度和磁性能的关系.实验中制备出的热压/热变形磁体的密度高达7.508 g·cm-3,磁体的磁能积为61 kJ·m-3.实验表明,温度是影响热压/热变形磁体性能的重要因素.磁体在平行于压力方向的磁性能稍高于垂直于压力方向的磁性能,体现出微弱的各向异性.
参考文献
[1] | 徐晖,倪建森,朱明原,周邦新,董远达.双相纳米晶Nd2Fe14B/α-Fe磁体的热稳定性研究[J].稀有金属,2003(05):645-646. |
[2] | 包小倩,周寿增,王佐诚,乔袆,张茂才,刘湘华.制备工艺对Pr2Fe14B/α-Fe纳米复合永磁材料组织与磁性的影响[J].中国稀土学报,2003(01):27-30. |
[3] | Coehoorn R et al.Novel permanent magnetic materials made by rapid quenching[J].Journal De Physique,1988,49:669. |
[4] | Kneller E.F.;Hawig R. .The exchange-spring magnet: a new material principle for permanent magnets[J].IEEE Transactions on Magnetics,1991(4):3588-3560. |
[5] | Skomski R;Coey J M D .Giant energy product in nanostructure phase magnets[J].Journal of Applied Physics,1994,76(10):7059. |
[6] | Skomski R .Aligned two phase magnets:permanent magnetism of the feature[J].Journal of Applied Physics,1994,76(10):7059. |
[7] | Manaf A et al.New nanocrystalline high-remanence Nd-Fe-B by rapid solidification[J].Journal of Magnetism and Magnetic Materials,1993,128:302. |
[8] | Ding J et al.Remanence enhancement in mechanically alloyed isotropic Sm7Fe93 nitride[J].Journal of Magnetism and Magnetic Materials,1993,124:L1. |
[9] | Zhang Xiangyi .Nanocomposite magnets and their preparation under higher pressure[J].Current Advances in Materials and Processes,2001,3:369. |
[10] | Zhang X Y et al.Crystallization kinetics and phase transition under high pressure of amorphous Sm8Fe85Si2C5 alloy[J].Acta Materialia,2001,49:3889. |
[11] | Mishra R K et al.The microstructure of hot deformed neodymium-iorn-born magnets with energy product with 48MGOe[J].Journal of Applied Physics,1993,73:647. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%