The cavitation erosion corrosion behaviour of ZQMn 12-8-3-2 manganese-nickel-aluminum bronze and ZHMn55-3-1 manganese-brass was investigated by mass loss, electrochemical measurements (polarization curves and electrochemical impedance spectroscopy) and the cavitation damaged surfaces were observed by scanning electron microscopy (SEM). The results showed that ZQMn 12-8-3-2 had better cavitation erosion resistance than ZHMn55-3-l. After the cavitation erosion for 6 h, the cumulative mass loss of ZQMnl2-8-3-2 was about 1/3 that of ZHMn55-3-l. The corrosion current density of ZQMnl2-8-3-2 was less than that of ZHMn55-3-l under both static and cavitaiton condition. The free-corrosion potentials of ZQMnl2-8-3-2 and ZHMn55-3-l were all shifted in positive direction under cavitation condition compared to static condition. In the total cu-mulative mass loss under cavitation condition, the pure erosion played a key role for the two tested materials (74% for ZHMn55-3-l and 60% for ZQMnl2-8-3-2), and the total synergism between corrosion and erosion of ZQMnl2-8-3-2 (39%) was larger than that of ZHMn55-3-l (23%). The high cavitation erosion resistance of ZQMnl2-8-3-2 was mainly attributed to its lower stacking fault energy (SFE), the higher microhardness and work-hardening ability as well as the favorable propagation of cavitation cracks for ZQMn 12-8-3-2, i.e., parallel to the surface rather than perpendicular to the surface for ZHMn55-3-l.
参考文献
| [1] | S. Z. Luo;Y. G. Zheng;M. C. Li .Effect of Cavitation on Corrosion Behavior of 20SiMn Low-Alloy Steel in 3 percent Sodium Chloride Solution[J].Corrosion: The Journal of Science and Engineering,2003(7):597-605. |
| [2] | A. Al-Hashem;W. Riad .The role of microstructure of nickel-aluminium-bronze alloy on its cavitation corrosion behavior in natural seawater[J].Materials Characterization,2002(1):37-41. |
| [3] | A. Al-Hashem;P-G- Caceres;W.T. Riad .Cavitation Corrosion Behavior of Cast Nickel-Aluminum Bronze in Seawater[J].Corrosion: The Journal of Science and Engineering,1995(5):331-342. |
| [4] | R. C. Barik;J. A. Wharton;R. J. K. Wood;K. S. Tan;K. R. Stokes .Erosion and erosion-corrosion performance of cast and thermally sprayed nickel-aluminium bronze[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2005(1):230-242. |
| [5] | C.H. Tang;F.T. Cheng;H.C. Man .Effect of laser surface melting on the corrosion and cavitation erosion behaviors of a manganese-nickel-aluminium bronze[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):195-203. |
| [6] | X.Y. Li;Y.G. Yan;L. Ma .Cavitation erosion and corrosion behavior of copper-manganese-aluminum alloy weldment[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):82-89. |
| [7] | W. Liu;Y. G. Zheng;C. S. Liu;Z. M. Yao;W. Ke .Cavitation erosion behavior of Cr-Mn-N stainless steels in comparison with 0Cr13Ni5Mo stainless steel[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2003(7/8):713-722. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%