采用B2O3-LiF-NaF助熔剂体系、中部籽晶法生长出BaAlBO3F2(BABF)晶体,对该晶体的弱吸收性能进行了表征.利用同步辐射白光X射线形貌术和化学腐蚀法研究了BABF晶体的缺陷,观察到BABF晶体中的主要缺陷是生长条纹和位错,并根据形貌和结构特点对生长条纹产生的原因进行了分析讨论,提出了一些减少缺陷和提高晶体质量的措施和方法.
参考文献
| [1] | Hu Z G;Yusuke M;Takatomo S et al.A New Nonlinear Optical Crystal-BaAlBO3 F2[J].Japanese Journal of Applied Physics,2002,41:1131-1133. |
| [2] | Zhang-Gui Hu;Masashi Yoshimura;Yusuke Mori;Takatomo Sasaki .Growth of a new nonlinear optical crystal―BaAlBO_3F_2[J].Journal of Crystal Growth,2004(3/4):287-290. |
| [3] | Huang H;Hu Z G;Chen C T et al.Ab Initio Calculations on the Borate Nonlinear Optical Crystal BaAlBO3 F2[J].Journal of Applied Physics,2009,106:1031071-1031075. |
| [4] | Yong Zhou;Guiling Wang;Yinchao Yue;Chengming Li;Yuanfu Lu;Dafu Cui;Zhanggui Hu;Zuyan Xu .High-efficiency 355 nm generation in barium aluminum borate diflouride (BaAlBO_(3)F_(2))[J].Optics Letters,2009(6):746-748. |
| [5] | Zhou Y;Hu Z G;Xu Z Y et al.Nonlinear Optical Properties of BaAlBO3F2 Crystal[J].Optics Express,2009,17(22):20033-20038. |
| [6] | 王晓丹,潘涛,臧涛成,马春兰,徐晓东,徐军,曾雄辉.Yb： Lu_3Al_5O_（12）晶体的生长及缺陷研究[J].人工晶体学报,2010(01):57-61. |
| [7] | 王英民,宁丽娜,彭燕,徐化勇,胡小波,徐现刚.6H-SiC成核表面形貌与缺陷产生的研究[J].人工晶体学报,2009(01):7-10,38. |
| [8] | Yue YC;Hu ZG;Chen CT .Flux growth of BaAlBO3F2 crystals[J].Journal of Crystal Growth,2008(6):1264-1267. |
| [9] | 岳银超,WANG Jia-nuo,胡章贵.大尺寸、高质量BaAlBO3F2晶体的生长[J].人工晶体学报,2008(04):777-780,824. |
| [10] | 许顺生;冯端.X射线衍衬貌相学[M].北京:科学出版社,1987:37-92. |
| [11] | Hu Z G;Yusuke M;Takatomo S et al.Reinvestigation of the Crystal Structure of Barium Aluminum Borate Diflouride,BaAlBO3 F2,a New Nonlinear Optical Material[J].Zeitschrift für Kristallographie-New Crystal Structures,2003,218:1-2. |
| [12] | 张克从;张乐潓.晶体生长科学与技术[M].北京:科学出版社,1997:639-721. |
| [13] | Keshra S.Etching of Crystals[M].Netherlands:North-Holland Physics Publishing Co,1987:302-339. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%