参照石灰吸收法,通过测定Ca(OH)2含量,分别研究了在无激发剂、不同浓度NaOH激发剂的情况下增钙煤矸石的火山灰性能.采用X射线衍射和汞压入法等测试方法对各种增钙煤矸石活性评价过程进行了结构层次上的分析.结果表明:各复合体系水化过程的结构特性与体系中Ca(OH)2含量的变化规律基本一致.
参考文献
| [1] | Xu A M;Shondeep L S .Microstructural study of gypsum activated fly ash hydration in cement pastes[J].Cement and Concrete Research,1991,21:1137. |
| [2] | 谷章昭;乐美龙 .粉煤灰的活性研究[J].硅酸盐学报,1982,10(02):152. |
| [3] | Shi C J .Early microstructure development of activated limefly ash pastes[J].Con Res,1996,26:1351. |
| [4] | Katz A .Microscopic study of alkali-activated fly ash[J].Cement and Concrete Research,1998,28:197. |
| [5] | Manjit S;Mridul G .Cementitious binder from fly ash and other industrial wastes[J].Cement and Concrete Research,1999,29:309. |
| [6] | 林秀 .粉煤灰的产物组成和常温下粉煤灰活性的研究[J].硅酸盐学报,1982,10(02):486. |
| [7] | Fan Y M;Yin S H;Wen Z Y et al.Activation of fly ash and its effects on cement properties[J].Cement and Concrete Research,1999,29:467. |
| [8] | Bryan K M;Robert L D .Pozzolanic and cementitious reactions of fly ash in blended cement pastes[J].Cement and Concrete Research,1988,18:301. |
| [9] | 邹海清.不同活化剂对粉煤灰活性激发的影响研究[J].采矿技术,2004(04):17-19,23. |
| [10] | 沈威;黄文熙;闵盘荣.水泥工艺学[M].武昌:武汉工业大学出版社,1991:184. |
| [11] | 杨启凯.分析化学实验[M].武昌:武汉工业大学出版社,1994:39. |
| [12] | 水泥化学分析方法[S].,1996. |
| [13] | 水泥工艺实验[M].,1995:108. |
| [14] | 杨南如.无机非金属材料测试方法[M].武昌:武汉工业大学出版社,1993:1. |
| [15] | 廉慧珍;童良;陈恩义.建筑材料物相研究基础[M].北京:清华大学出版社,1996:105. |
| [16] | 宋旭艳,宫晨琛,李东旭.煤矸石活化过程中结构特性和力学性能的研究[J].硅酸盐学报,2004(03):358-363. |
| [17] | 宋旭艳,李东旭.不同活化方法对煤矸石胶凝性能的影响[J].材料导报,2004(03):99-102. |
| [18] | 李东旭 .高掺量矿渣、磷渣生态水泥的研究[D].南京:南京工业大学,1998. |
| [19] | 李东旭;毛良喜;吴学权 .外加剂对高掺量磷渣水泥的强度和孔结构性能的影响[J].南京工业大学学报(自然科学版),1998,20(02):44. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%