利用加速腐蚀实验方法研究了腐蚀对一种亚共析铀铌合金拉伸性能的影响,并用SEM和EDS对拉伸试样的组织结构、成分、表面形貌和断口形貌进行了分析.腐蚀实验表明:随着腐蚀时间的增加,拉伸试样表面的腐蚀程度加剧,经过约180 d的腐蚀后,试样表面形成了腐蚀斑,其大小为50μm左右;力学拉伸测试表明:在实验范围内,合金的屈服强度和抗拉强度无明显变化,而试样的延伸率及断面收缩率则有下降的趋势.断口形貌表明,合金在实验范围内腐蚀后,其断裂方式仍以韧性断裂为主.此外,对引起合金力学性能变化的主要因素也进行了探讨.
参考文献
| [1] | Wilkinson W D.Uranium Metallurgy[M].New York:Interscience Publishers,1962 |
| [2] | Burke J J;Coiling D A;Gorum A E.Physical Metallurgy of Uranium Alloys[M].Brook Hill Publishing Company,1976 |
| [3] | Jackson R J .Mechanical Properties of Conanuously Cooled Uranium-2.4 Weight Percent Niobium Alloy[RFP-3040][R].USA:Rockwell International Corp,1981. |
| [4] | Jackson R J .Reversible Martensitic Transformations Between Transition Phases of Uranium-Base Niobium Alloys[RFP-1535][R].USA:Dow Chemical Corp,1970. |
| [5] | Beevers C J;Newman G T .[J].Journal of Nuclear Materials,1967,23:10. |
| [6] | Jackson R J .Effect of Humidity on Tensile Ductility of Uranium-Titanium[RFP-2048][R].USA:Dow Chemical Corp,1972. |
| [7] | Hughes A N;Orman S;Picton G et al.[J].Journal of Nuclear Materials,1969,33:165. |
| [8] | 曾力,杨淑慧,张(龙天).受腐蚀钢筋力学性能的试验研究[J].河南科学,2005(06):877-879. |
| [9] | 刘家慧,刘立新.腐蚀对钢筋力学性能影响的试验研究[J].平原大学学报,2003(04):35-37. |
| [10] | Kermanidis A T;Labeas G;Pantelakis S G.[A].Montreal,Canada,2005 |
| [11] | Pantelakis SG.;Apostolopoulos CA.;Daglaras PG. .Tensile and energy density properties of 2024, 6013, 8090 and 2091 aircraft aluminum alloy after corrosion exposure[J].Theoretical and Applied Fracture Mechanics,2000(2):117-134. |
| [12] | Kermanidis AT;Petroyiannis PV;Pantelakis SG .Fatigue and damage tolerance behaviour of corroded 2024 T351 aircraft aluminum alloy[J].Theoretical and Applied Fracture Mechanics,2005(1):121-132. |
| [13] | Mon C O;Lee S B .[J].Oxidation of Metals,1993,39:1. |
| [14] | 杨江荣,汪小琳,周萍,何立峰,郎定木.氧化对U-2.5wt%Nb合金拉伸性能的影响研究[J].核科学与工程,2007(03):259-264. |
| [15] | Kollie T G;Anderson R C;Carpenter D A et al.[J].Journal of Nuclear Materials,1984,125:160. |
| [16] | Armstrong P E .Effect of Hydrogen on the Mechanical Properties of U-5.7wt%Nb[LA-9870][R].USA:Los Alamos National Lab,NM(USA),1983. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%