通过正交试验考察了水性环氧丙烯酸酯、水性聚氨酯丙烯酸酯和水性活性稀释剂的不同用量对光固化涂层性能的影响。结果表明：水性环氧丙烯酸酯与水性聚氨酯丙烯酸酯配比为3∶7，水性活性稀释剂用量为12%时，涂层的力学性能优异，涂层凝胶率超过90%，吸水率为2.36%，击穿强度达到100 MV/m。
The effects of different dosage of waterborne epoxy acrylate, waterborne urethane acrylate and aqueous reactive diluent on the properties of UV curable coating were investigated by orthogonal test. The results show that when the ratio of waterborne epoxy acrylate and waterborne polyurethane acrylate is 3∶7, the dosage of aqueous reactive diluent is 12%, the mechanical properties of the coating is excellent, the gel ratio is more than 90%, the water absorption is 2.36%, and the breakdown strength attains 100 MV/m.
参考文献
| [1] | 陈乐培,王海杰,武志明.光敏树脂及其紫外光固化涂料发展新动向[J].热固性树脂,2003(05):33-36. |
| [2] | 姚永平,崔艳艳,董智贤,刘晓暄.水性光固化涂料研究进展[J].涂料工业,2011(08):74-79. |
| [3] | 徐超,王德海.紫外光固化水性体系研究进展[J].轻工机械,2010(01):1-4. |
| [4] | 魏丹,叶代勇,黄洪,陈焕钦.多重交联紫外光固化水性聚氨酯涂料[J].涂料工业,2008(05):4-7. |
| [5] | 艾照全,周雪松.紫外光固化水性涂料综述[J].涂料技术与文摘,2007(02):1-4. |
| [6] | 狄宁宇,曹万荣,沈鉴峰,祝阳.水性环氧树脂涂料的最新研究进展[J].绝缘材料,2009(04):27-30. |
| [7] | 邹海良,张亚峰,邝健政,刘军,徐宇亮.具有长疏水链基型水性环氧固化剂的乳化性质及其涂膜的热学性能[J].绝缘材料,2010(03):51-54. |
| [8] | 李红强,曾幸荣.紫外光固化水性涂料的研究进展[J].中国涂料,2007(05):28-32. |
| [9] | 何琰洁.环保水性涂料的研究进展[J].科技信息,2012(02):352-353. |
| [10] | 王韬,曾光明,陈能昌,陈晓锐,温晋嵩.水性UV涂料的研究进展[J].广州化工,2009(04):23-24,38. |
| [11] | 艾照全,周雪松.紫外光固化水性涂料综述[J].涂料技术与文摘,2007(02):1-4. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%