用XRD、SEM、ESR结合常规电性能测试手段,研究了锰掺杂对两类大功率PZT材料微结构及压电性能的影响.结果表明:随着锰含量的增大,三角晶相含量增多,准同型相界相应向四方相移动.锰在PZT材料中主要以Mn2+和Mn3+的方式共存.锰在PZT陶瓷材料中"溶解度"约为1,5mol%.添加少量的锰有利于PZT材料晶粒的长大及压电性能的改善,而过量的锰则会在晶界积聚,抑制晶粒的长大,并使材料的压电性能恶化.对两类大功率材料PZTS和PZTM而言,锰的最佳添加量分别为0.75mol%及0.25mol%.
参考文献
| [1] | Xu Y H .Ferroelectric Material and Their Applications[Z].University of Califoria Los Angels,CA,USA,North Holland,1991. |
| [2] | 张沛霖;钟维烈.压电材料与器件[M].济南:山东科学出版社,1997 |
| [3] | Eyraud S;Gonnard P;Troceaz M .[J].Ferroelectrics,1989,93:127. |
| [4] | Takahashi S .[J].Ferroelectrics,1982,41:143. |
| [5] | Katiyar V K;Srivatava S L;Singh J .[J].Ferroelectrics,1997,193:21. |
| [6] | Mabvd S A .[J].Journal of Applied Crystallography,1980,13:21. |
| [7] | Hahn L;Vchino K;Nomvra S .[J].Japanese Journal of Applied Physics,1978,17:634. |
| [8] | NG Y S;Alexander S M .[J].Ferroelectrics,1983,51:81. |
| [9] | Kamiya T;Suzuki T;Tsurami T et al.[J].Japanese Journal of Applied Physics,1992,31:3058. |
| [10] | Bykov I P;Glinchvk M D M;Skorokhod V V .[J].Ferroelectrics,1992,127:89. |
| [11] | 裘祖文.电子自旋共振谱[M].北京:科学出版社,1980 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%