High temperature oxidation behaviors of FGH96 P/M superalloy have been studied in air at temperatures ranging from 600 to 1000℃. By means of isothermal oxidation testing,X-ray diffraction, SEM (scanning electron microscopy), and EDS (energy dispersive X-ray spectroscopy) analyses, the oxidation kinetics as well as the composition and morphology of scales were investigated. Thermodynamic calculations were used to explain the oxidation mechanism. The results showed that as the oxidation temperature increased, the oxidation rate, the scale thickness, and scale spallation increased. FGH96 P/M superalloy exhibits good oxidation resistance at temperature below 800 ℃. The oxidation kinetics follows an approximately parabolic rate law, and the oxide layer was mainly composed of Cr2O3, TiO2,and a little amount of NiCr2O4. The oxidation is controlled by the transmission of chromium,titanium, and oxygen through the oxide scale.
参考文献
| [1] | G B Viswanathanl;P Sarosil;M Henry.[A].TMS,Warrendale,2004:173. |
| [2] | S Y Wang;H Q Li;M C Zhang.[J].Hot Working Technology,2002(06):16. |
| [3] | D D Whitis.[A].TMS,Warrendale,2004:391. |
| [4] | Y H Liu;F G Li;S C Wu .[J].Acta A eronautica et A stronautica Sinica,2003,24:278. |
| [5] | Y B Ching;J L Yi;H K Chun .[J].Surface and Coatings Technology,2004,183:74. |
| [6] | S Sinharoy;S L Narasimhan.[A].TMS,Warrendale,2004:623. |
| [7] | W Gao;Z W Li;Z Wu .[J].Intermetallics,2002,10:263. |
| [8] | W M Guo;D Feng;F G Zhang .[J].Journal of Iron and Steel Research,2002,14:17. |
| [9] | W M Guo;F G Zhang;Y W Zhang.[J].Powder Metallurgy Industry,2002(12):30. |
| [10] | C.F.Miller;G.W.Simmons .High temperature oxidation of Nb, NbC and Ni_3Nb and oxygen enhanced crack growth[J].Scripta materialia,2000(3):227-232. |
| [11] | S X Zhao;X S Xie;G D Smith .[J].Surface and Coatings Technology,2004,185:178. |
| [12] | M J Lia;X F Suna;H R Guana .[J].Surface and Coatings Technology,2004,185:172. |
| [13] | R Haugsrud .[J].Materials Science and Engineering A-structural Materials Properties Microstructure and Processing,2001,298:216. |
| [14] | J Kl(o)wer;U Brill;U Heubner .[J].INTERMETALLICS,1999,7:1183. |
| [15] | F H Yuan;Y S Yoo;C Y Jo .[J].Surface and Coatings Technology,2004,183:106. |
| [16] | J P Calder6n;E B Figueroa;J G Gonzalez-Rodriguez .[J].Materials Letters,1999,38:45. |
| [17] | D P Whittle;D Coutsouradis;P Felix;H.Fischmeister,L.Habraken,Y.Linblom,M.O.Speidel.Applied Science[M].London,1978:109. |
| [18] | P Felix;A B Hart;A J B Cutler.Applied Science[M].London,1972:331. |
| [19] | D.B. Lee;S.W. Woo .High temperature oxidation of Ti-47 percent Al--1:7 percent Vv-3.7 percent Zr alloys[J].Intermetallics,2005(2):169-177. |
| [20] | D B Lee;M H Kim;Y C Lee .[J].Surface and Coatings Technology,2001,141:232. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%