本文通过监测添加不同类型和不同比例的抗氧剂的紫外光固化材料在热老化过程中黄变因数的变化,来考察抗氧剂对紫外光固化材料热老化黄变的影响和不同的抗黄变能力.利用紫外-可见光谱仪表征老化过程试样的透光率,结果表明,抗氧剂能很好地减小紫外光固化材料的热老化黄变,抗氧剂中的羟基的抗黄变能力存在差异,决定了抗氧剂的抗黄变能力.Irgafos-168分别与Irganox-1010和Irganox-1076复配时,表现出较好的协同效应,从而使复配抗氧剂的抗黄变能力比单组分抗氧剂的抗黄变能力强.
参考文献
| [1] | Popovic, IG;Katsikas, L;Velickovic, JS .The non-oxidative thermal degradation of poly(di-n-alkyl itaconates). I. Analysis of the thermolysis volatiles[J].Polymer Degradation and Stability,2005(1):153-164. |
| [2] | Atkinson, J.L.;Vyazovkin, S. .Non-oxidative thermal degradation of poly(glycidol), poly(glycidol)-g-L- lactide, and poly(glycidol)-g-glycolide[J].Macromolecular chemistry and physics,2011(19):2103-2113. |
| [3] | Audouin L;Gucguen V;Tcharkhtchi A et al."Close loop” mechanistic schemes for hydrocarbon polymer oxidation[J].Journal of Polymer Science Part A:Polymer Chemistry,1995,33(06):921-927. |
| [4] | Franks F;Gent M;Roberts B .Quantitative study of the oxidative discoloration of ethyl linoleate.Ⅲ.Some kinetic aspects of the early stages of the hydroperoxidation reaction[J].Journal of Applied Chemistry,1965,15(06):243-249. |
| [5] | 刘景军,李效玉.高分子材料的环境行为与老化机理研究进展[J].高分子通报,2005(03):62-69. |
| [6] | 马剑英,谭志勇,曹春雷,杨海东,张会轩.抗氧剂对PMMA树脂的热稳定作用[J].中国塑料,2009(03):86-89. |
| [7] | 王玲,胡世伟,云高杰,温晓萌,丁著明.环氧树脂降解与稳定化研究进展[J].热固性树脂,2009(03):46-51. |
| [8] | 张新兰,李博,张琴,傅强,周楠.含抗氧剂聚碳酸酯的制备及降解性能研究[J].塑料工业,2009(01):49-52. |
| [9] | 胡行俊.抗氧剂[M].北京:国防工业出版社,2009 |
| [10] | 朱福海.高分子材料变黄程度的测定[J].合成材料老化与应用,1999(03):34. |
| [11] | 杨建文;曾兆华;陈用烈.光固化涂料及应用[M].北京:化学工业出版社,2004:361-363. |
| [12] | 王刚,王鉴,王立娟,辛明瑞.抗氧剂作用机理及研究进展[J].合成材料老化与应用,2006(02):38-42. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%