采用自制的低碳Ti、B微合金化金属芯焊丝进行了金属零件的堆焊快速成形试验,研究了成形件的组织特征和显微硬度,结果表明:沿沉积高度方向上,成形件的连续组织具有分层特征,珠光体的含量逐渐减少,铁素体的含量逐渐增加,表层主要为块状铁素体,这与成形件各区域的热循环条件和基板材料中C元素的扩散有关;成形件底部和中间区域的显微硬度显著高于表层区域的显微硬度.采用纳米压痕法研究了成形件组织中针状铁素体和块状铁素体的微观力学性能,结果表明:针状铁素体的硬度是块状铁素体的1.28倍,两者的弹性模量相当.因此,获得大量的针状铁素体组织是提高成形件力学性能的重要途径.
The experiment for manufacturing mild-steel parts by surfacing rapid forming with self-made low carbon Ti,B microalloyed metal cored wires Was carried out.The microstructure and microhardness of the part were studied.The results indicate that along deposition height direction,the mierostructure of the parts shows layered characteristics,the amount of pearlite decreases and the amount of ferrite increases,and the surface zone is mostly composed of massive ferrite.The formation of the microstructure related to the different thermal cycle conditions of each zone in the part and diffusion of carbon from base plate.The microhardness of bottom and middle zones is much higher than that of surface zone.The micro mechanical properties of acicular ferrite and massive ferrite were investigated by nanoindentation technology.The results show that the hardness of acicular ferrite is 1.28 times of that of massive ferrite,and Young's modulus of the both ferrite is equivalent.Therefore,it is favourable for high proportion of aeicular ferrite in the microstructure to enhance mechanical properties of surfacing forming parts.
参考文献
| [1] | Yu Ming Zhang;Pengjiu Li;Yiwei Chen;Alan T. Male .Automated system for welding-based rapid prototyping[J].Mechatronics: The Science of Intelligent Machines,2002(1):37-53. |
| [2] | Kassmaul K;Schoch F W;Lucknow H.High quality large components shape welded by a SAW process[J].Welding Journal,1983(09):17-24. |
| [3] | McAninch M D;Conrardy C C .Shape melting a unique near-net shape manufacturing process[J].Welding Review International,1991,10(01):33-40. |
| [4] | Ribeiro F. .3D printing with metals[J].Control & automation,1998(1):31-38. |
| [5] | YuMing Zhang;Yiwei Chen;Pengjiu Li .Weld deposition-based rapid prototyping: a preliminary study[J].Journal of Materials Processing Technology,2003(2/3):347-357. |
| [6] | SONG Y A;Park S;Choi D et al.3D welding and milling:Part Ⅰ-a direct approach for freeform fabrication of metallic prototypes[J].International Journal of Machine Tools and Manufacture,2005,45:1057-1062. |
| [7] | SONG Y A;Park S;Chae SW .3D welding and miring:part Ⅱ-optimization of the 3D welding processusing an experimental design approach[J].International Journal of Machine Tools and Manufacture,2005,45:1063-1069. |
| [8] | 李建海,陈邦固.新型金属芯药芯焊丝的开发和应用[J].焊接技术,2001(03):47-50. |
| [9] | 余圣甫,余阳春,谢明立,李志远.二次热循环对晶内铁素体的影响[J].焊接学报,2003(02):89-92,96. |
| [10] | Babu SS .The mechanism of acicular ferrite in weld deposits[J].Current opinion in solid state & materials science,2004(3/4):267-278. |
| [11] | 礼宾,王核源,张舒庆.Ti、B微量元素对焊缝金属韧性的影响[J].机械工程材料,2003(01):32-34,43. |
| [12] | 王红美,徐滨士,马世宁,董世运.纳米Al2O3颗粒增强镍基复合镀层的制备及微观力学性能[J].材料热处理学报,2005(01):81-85. |
| [13] | 吴开明,张莉芹,贺信莱,尚成嘉,杨善武,王学敏.低碳微合金钢中针状铁素体的微观力学性能及其组织稳定性[J].金属学报,2006(01):19-22. |
| [14] | Ming-Chun Zhao;Ke Yang;Yi-Yin Shan .Comparison on strength and toughness behaviors of microalloyed pipeline steels with acicular ferrite and ultrafine ferrite[J].Materials Letters,2003(9/10):1496-1500. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%