借助于X射线衍射仪、声速取向度测量仪、扫描电镜、小角X光散射仪等研究了凝胶化聚丙烯腈(PAN)纤维的聚集态结构和形态结构特点.结果表明,与常规高温凝固和低温凝固成型方式得到的PAN纤维相比,凝胶化凝固形成的初生纤维和原丝晶粒尺寸小,在牵伸相同的情况下,凝胶化凝固原丝取向结构最高,表明其结构对张力的响应性较好;凝胶化凝固的PAN初生纤雏截面结构致密、内外均匀,表面沟槽深且均匀规则,凝胶化凝固的原丝微孔相对体积含量最小.
参考文献
| [1] | Hou C;Liang Y;Wang CG .Determination of the diffusion coefficient of H2O in polyacrylonitrile fiber formation[J].Journal of Polymer Research,2005(1):49-52. |
| [2] | Dong XG;Wang CG;Bai YJ;Cao WW .Effect of DMSO/H2O coagulation bath on the structure and property of polyacrylonitrile fibers during wet-spinning[J].Journal of Applied Polymer Science,2007(3):1221-1227. |
| [3] | 林凤崎,徐樑华,李常清,姚红.凝固条件对PAN初生纤维微孔结构形态的影响[J].合成纤维工业,2006(01):16-19. |
| [4] | Stephen Dalton;Frank Heatley;Peter M. Budd .Thermal stabilization of polyacrylonitrile fibres[J].Polymer: The International Journal for the Science and Technology of Polymers,1999(20):5531-5543. |
| [5] | 曾小梅,Jan Ellinger,张幼维,赵炯心,潘鼎.紫外分光光度法测定PAN纤维中的DMSO含量[J].合成纤维工业,2006(03):40-41. |
| [6] | 徐樑华,吴红枚.PAN/DMSO干湿法纺丝凝固工艺的研究[J].高分子材料科学与工程,2000(06):163-166. |
| [7] | 李常清,蓝雁,徐樑华.凝固条件对PAN初生纤维微结构的影响[J].合成纤维工业,2008(04):22-24. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%