以稀土合金为基体,探讨了在酸性的AlCl3-EMIC(2:1)室温熔盐中电沉积铝镀层的可能性,重点研究了稀土合金前处理工艺对镀层的影响.用SEM、EDS及XRD对电沉积前后的试样表面及界面进行了微观分析,用划格撕扯法对镀层与基体的结合力进行测定.结果表明,可以通过室温熔盐电沉积的方法,在稀土合金表面电沉积Al镀层;且对稀土合金表面在煤油中进行前处理,可防止稀土氧化膜的产生,并能得到均匀致密、结合良好的铝镀层;在电流密度2A/dm2,沉积时间2500 s条件下,可得到颗粒大小约10μm、厚度17μm的纯铝层,电流效率接近100%.对稀土合金表面电沉积Al机制进行了讨论.
参考文献
| [1] | 罗丽珠,汪小琳,伏晓国,赵正平,刘春荣.金属Ce表面氧化物的真空稳定性[J].核化学与放射化学,2007(02):75-79. |
| [2] | Gschneidner Jr K A;Pecharsky V K .[J].Journal of Rare Earths,2006,24(06):641. |
| [3] | Song L;Wang Y;Lin W et al.[J].Surface and Coatings Technology,2008,202(21):5146. |
| [4] | Izumi H;Machida K;Iguchi M et al.[J].Journal of Alloys and Compounds,1997,261:304. |
| [5] | Gray J E;Luan B .[J].Journal of Alloys and Compounds,2002,336(1-2):88. |
| [6] | 王庆富,张鹏程,鲜晓斌.铀及铀合金的防腐蚀电镀层研究进展[J].腐蚀与防护,2003(12):513-517. |
| [7] | 赖新春,陆雷,刘柯钊,杨江荣.金属铀真空原位断裂表面初期氧化研究[J].稀有金属材料与工程,2004(11):1182-1185. |
| [8] | Takahashi S;Koura N;Kohara S et al.[J].Plasmas&Ions,1999,2(13):91. |
| [9] | Chang JK;Chen SY;Tsai WT;Deng MJ;Sun IW .Electrodeposition of aluminum on magnesium alloy in aluminum chloride (AlCl3)-1-ethyl-3-methylimidazolium chloride (EMIC) ionic liquid and its corrosion behavior[J].Electrochemistry communications,2007(7):1602-1606. |
| [10] | 韩文生,谢锐兵,萧以德.钕铁硼稀土永磁材料室温熔盐电镀铝的研究[J].材料保护,2005(10):1-4. |
| [11] | 长崎诚三;平林真;刘安生.二元合金状态图集[M].北京:冶金工业出版社,2004:107. |
| [12] | 任清波,张鹏程,褚明福,龚伟平.Ce-5%La合金表面氧化过程研究[J].中国稀土学报,2007(06):730-735. |
| [13] | Luo L;Wang X;Fu X et al.[J].Journal of Rare Earths,2004,22(12):22. |
| [14] | Dakhel AA .Structural and ac electrical properties of oxidised La and La-Mn thin films grown on Si substrates[J].Materials Chemistry and Physics,2007(2/3):266-270. |
| [15] | Carlin R T;Crawford W;Bersch M .[J].Journal of the Electrochemical Society,1992,139(10):2720. |
| [16] | Jiang T;Brym MJC;Dube G;Lasia A;Brisard GM .Electrodeposition of aluminium from ionic liquids: Part I - electrodeposition and surface morphology of aluminium from aluminium chloride (AlCl3)-l-ethyl-3-methylimidazolium chloride ([EMIm]Cl) ionic liquids[J].Surface & Coatings Technology,2006(1/2):1-9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%