采用X射线衍射(XRD)、X射线荧光光谱分析(XRF)测试了失效电解铜箔用钛阳极表面结垢成分，考察了BH?阳极除垢剂对电解铜箔用钛阳极表面结垢的去除效果，通过循环伏安曲线、极化曲线、强化寿命测试分析了 BH?阳极除垢剂对钛阳极电催化活性的影响，给出了电解铜箔用钛阳极在应用过程中的维护措施。结果表明，BH?阳极除垢剂可以有效去除结垢而不会破坏钛阳极表面的贵金属涂层，有利于延长钛阳极的寿命。
The composition of scale formed on surface of failure titanium anode used for manufacturing of electrolytic copper foils was examined by X-ray diffraction (XRD) and X-ray fluorescence analysis (XRF). The effectiveness of BH anode descaling agent on the oxide-titanium anode used for electrolytic copper foils was studied and its influence on electrocatalytic activity of the anode was analyzed through cyclic voltammetry, polarization curve measurement, and accelerated service life test. The maintenance methods for oxide-coated titanium anode during the manufacturing of electrolytic copper foils were presented. The results indicated that the BH anode descaling agent removes the scales effectively, and has no damage to the precious metal oxide coating, extending the service life of the oxide-coated titanium anode.
参考文献
| [1] | 李文康.电解铜箔制造技术探讨[J].上海有色金属,2005(01):16-20. |
| [2] | 张招贤;赵国鹏;罗小军.钛电极学导论[M].北京:冶金工业出版社,2008:613. |
| [3] | 李俊,张震.电解铜箔添加剂研究进展[J].化学研究,2010(06):91-95. |
| [4] | 简志超.电解铜箔用IrO2+Ta205涂层钛阳极失效与维护[J].科技研究,2013(11):154-155. |
| [5] | 徐海清,胡耀红,陈力格,钟洪胜,张招贤.SnO2掺杂IrO2-Ta2O5涂层阳极的电催化活性及稳定性[J].电镀与涂饰,2014(06):267-270. |
| [6] | COMNINELLIS CH;VERCESI G P .Characterization of DSA?-type oxygen evolving electrodes:choice of a coating[J].Journal of Applied Electrochemistry,1991,21(04):335-345. |
| [7] | 胡吉明,朱艳冗,孟惠民,孙冬柏,吴继勋,杨德钧.钛基IrO2-Ta2O5涂层阳极电化学多孔性研究[J].稀有金属,2000(05):345-348. |
| [8] | 胡吉明,孟惠民,张鉴清,曹楚南.Ti基IrO2+Ta2O5阳极在H2SO4溶液中的电解时效行为[J].物理化学学报,2002(01):14-20. |
| [9] | 姚书典,沈嘉年,刘冬,吴志良,孙娟.涂层IrO2+Ta2O5钛阳极在析氧过程中的形貌和成分变化[J].贵金属,2006(04):12-17. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%