以Ni60A自熔合金粉末和镍包碳化钨粉末为原料,利用真空熔覆方法在低碳钢表面制备了镍基碳化钨耐磨复合涂层.研究了真空工艺条件下,镍基合金中碳化钨颗粒的转变行为.试验结果表明,高温下保温时间延长对镍基碳化钨复合涂层的组织影响很大,WC颗粒在镍基体中发生转变,转变的主要特征是WC硬质相边缘转变为针状相,随着高温加热时间的延长,针状相组织面积扩大,转变为针状团簇结构,最终转变为粒状相.结合XRD分析,粒状相为具有复杂立方结构的Fe6W6C相,这种碳化物,显著降低了涂层的硬度.
参考文献
| [1] | 宫文彪,杜辉,孙大千.WC颗粒增强Ni基合金涂层的组织与性能[J].金属热处理,2006(02):26-29. |
| [2] | 黄新波,贾建援,林化春.钴基合金-碳化钨复合涂层的耐蚀性能[J].机械工程材料,2003(11):49-51. |
| [3] | 曲仕尧,王新洪,邹增大,刘雪梅.WC硬质合金颗粒堆焊烧损的机理[J].焊接学报,2001(02):85-88. |
| [4] | Verdon C.;Martin JL.;Karimi A. .A study of high velocity oxy-fuel thermally sprayed tungsten carbide based coatings. Part 1: Microstructures[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):11-24. |
| [5] | Kear B H et al.[J].Scripta Materialia,2001,44(08):1703. |
| [6] | Stewart DA.;McCartney DG.;Shipway PH. .Influence of heat treatment on the abrasive wear behaviour of HVOF sprayed WC-Co coatings[J].Surface & Coatings Technology,1998(1/2):13-24. |
| [7] | Li H;Khor KA;Yu LG;Cheang P .Microstructure modifications and phase transformation in plasma-sprayed WC-Co coatings following post-spray spark plasma sintering[J].Surface & Coatings Technology,2005(1):96-102. |
| [8] | 索进平,冯涤,骆合力,崔崑.WC颗粒在堆焊过程中溶解机理的研究[J].功能材料,2003(02):221-223. |
| [9] | Stewart D A et al.[J].Acta Materialia,2000,48(07):1593. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%