以聚乙二醇（PEG）为致孔剂,利用自由基聚合法制备了具有多孔结构的半纤维素接枝共聚丙烯酰胺水凝胶,分别用FT-IR和SEM对水凝胶的结构和表面形态进行了分析;研究了水凝胶的pH值敏感性以及单体比例、PEG用量、PEG分子量和交联剂对溶胀率的影响;最后,以亚甲基蓝为模型药物研究了该水凝胶对药物的释放性能。实验结果表明,PEG为致孔剂,没有参与聚合反应;该水凝胶具有多孔结构以及优良的pH值敏感性,能够实现药物的控制释放,有望成为一种良好的药物载体。
In this paper, porous hemicellulose-grafted-po]y （acrylamide） hydrogels were prepared using PEG as porogen and free radical polymerization. The structure and surface morphology of these hydrogels were analyzed by FT-IR and SEM. pH-sensitive of hydrogels and effects of monomer ratio, amount of PEG, PEG molecular weight and cross-linking on equilibrium swelling ratio were also discussed. Finally, release performance of hydrogels using methylene blue as model drug was studied. These experimental results indicated that the porogen PEG was not the polymerization; the hydrogels had porous structure and excellent pH-sensitivity, which was expected to become a good drug carrier.
参考文献
| [1] | A.K.Bajpai;Anjali Giri .Water sorption behaviour of highly swelling (carboxy methylcellulose-g-polyacrylamide) hydrogels and release of potassium nitrate as agrochemical[J].Carbohydrate Polymers: Scientific and Technological Aspects of Industrially Important Polysaccharides,2003(3):271-279. |
| [2] | Xiaogang Luo;Shilin Liu;Jinping Zhou .In situ synthesis of Fe3O4/cellulose microspheres with magnetic-induced protein delivery[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2009(21):3538-3545. |
| [3] | Mei-Ju Yang;Chun-Hung Chen;Pei-Ju Lin .Novel Method of Forming Human Embryoid Bodies in a Polystyrene Dish Surface-Coated with a Temperature-Responsive Methylcellulose Hydrogel[J].Biomacromolecules,2007(9):2746-2752. |
| [4] | Sun XF;Sun RC;Fowler P;Baird MS .Extraction and characterization of original lignin and hemicelluloses from wheat straw[J].Journal of Agricultural and Food Chemistry,2005(4):860-870. |
| [5] | Sun Xiaofeng;Xu Feng;Sun Runcang et al.Characteristies of degraded hemicellulosic polymers obtained from steam exploded wheat straw[J].Carbohydrate Polymers,2005,60(01):15-26. |
| [6] | Dace R;McBride E;Brooks K;Gander J;Buszko M;Doctor VM .Comparison of the anticoagulant action of sulfated and phosphorylated polysaccharides.[J].Thrombosis Research: An International Journal on Vascular Obstruction, Hemorrhage and Hemostasis,1997(1):113-121. |
| [7] | 卢国冬,燕青芝,宿新泰,刘中清,葛昌纯.多孔水凝胶研究进展[J].化学进展,2007(04):485-493. |
| [8] | 杨桔,霍丹群,侯长军,杨眉,张国平,张玉婵,董家乐.冷冻聚合法制备多孔P（NIPAm-Co-AAm）水凝胶及其性能研究[J].功能材料,2011(02):343-346,350. |
| [9] | Mohan YM;Murthy PSK;Raju KM .Preparation and swelling behavior of macroporous poly(acrylamide-co-sodium methacrylate) superabsorbent hydrogels[J].Journal of Applied Polymer Science,2006(5):3202-3214. |
| [10] | Ecaterina Stela Dragan;Diana Felicia Apopei.Synthesis and swelling behavior of pH-sensitive semi-interpenetrating polymer network composite hydrogels based on native and modified potatoes starch as potential sorbent for cationic dyes[J].Chemical engineering journal,2011:252-263. |
| [11] | 李智慧,刘文涛,李中原,张鸿儒,杨明成,何素芹,朱诚身.PNIPA/PEG多孔智能水凝胶的辐射合成与性能研究[J].功能材料,2009(12):2047-2049,2057. |
| [12] | 张建涛,黄世文,汪璐玲,卓仁禧.快速响应大孔聚（N-异丙基丙烯酰胺-co-丙烯酸）水凝胶的合成及表征[J].高等学校化学学报,2004(12):2370-2374. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%