利用饱和羟基硅烷为改性剂、钛酸丁酯为催化剂,以1,2-丙二醇与己二酸进行缩聚反应,制备了改性醇酸型聚酯树脂.研究了反应条件对反应转化率的影响,确定了适宜的合成工艺条件.当n(1,2-丙二醇):n(己二酸)=1.3:1,硅醇、三(2-羟乙基)异氰尿酸酯(THEIC)和钛酸丁酯的用量分别为3%、5.6%和0.2%时,在200.C下缩聚反应5 h,可得到无色透明的聚酯树脂,其转化率达到94.8%,黏度900 mPa·s,表面张力(20°C下)27 mN/m.树脂经固化后所得漆膜的附着力1级、冲击强度4.5MPa、硬度2H.
参考文献
| [1] | Chuanguang Wang;Cheng Zhang;Michael S. Lee;Larry R. Dalton;Hua Zhang;William H. Steier .Urethane-Urea Copolymers Containing Siloxane Linkages: Enhanced Temporal Stability and Low Optical Loss for Second-Order Nolinear Optical Applications[J].Macromolecules,2001(7):2359-2363. |
| [2] | Kumar SA.;Narayanan TSNS. .Thermal properties of siliconized epoxy interpenetrating coatings [Review][J].Progress in Organic Coatings: An International Review Journal,2002(4):323-330. |
| [3] | 王旭波,赵士贵,杨欣欣,王峰,东青.有机硅改性聚酯树脂的研究进展[J].有机硅材料,2006(05):264-267. |
| [4] | Lin LH;Chen KM .Surface activity and water repellency properties of cleavable-modified silicone surfactants[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2006(1/3):99-106. |
| [5] | 冯林林,张兴元,戴家兵,葛震,潮静,白晨艳.有机硅改性聚氨酯的合成及其表面性能[J].高分子材料科学与工程,2007(03):47-50. |
| [6] | 汪杰,贾延华,张鑫,张东.己二酸与1,2-丙二醇或1,4-丁二醇自催化酯化反应的动力学研究[J].聚酯工业,2009(01):19-22. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%