采用不同焊接工艺参数对X100管线钢进行焊接试验,并对母材进行微观组织观察及宏观力学特性测试,对比分析X100管线钢母材和经历不同焊接热过程后所得焊缝的微观组织及宏观力学特性.结果表明:经历不同焊接热过程后的X100管线钢焊缝组织比母材组织粗大,主要为无碳贝氏体；冲击韧性比母材略高；抗拉强度和屈服强度与母材基本保持一致.
参考文献
| [1] | Okaguchi S.Production and development of X100 and X120 grade line pipes[A].,2005 |
| [2] | 罗海文,董瀚.高级别管线钢X80～X120的研发与应用[J].中国冶金,2006(04):9-15. |
| [3] | Dhua S K;Mukerjee D;Sarma D S .Influence of thermomechanicl treatments on the microstructure and mechanical orpperties of HSLA-100 steel plates[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2003,34(02):241-253. |
| [4] | 王路兵,武会宾,任毅,张鹏程,唐荻.终冷温度对X100管线钢组织与性能的影响[J].热加工工艺,2007(14):21-23,26. |
| [5] | Shuji Okaguchi .Production and development of linepipe steel in grade X100 and X120[R].X100/X120 High Strength Line Pipe International Forum,Beijing,2005. |
| [6] | 齐丽华,杨龙,冯耀荣,张建勋.X100级管线钢的微观组织与力学性能的关系[J].热加工工艺,2011(02):15-19. |
| [7] | 严春妍,李午申,冯灵芝,薛振奎,白世武,刘方明.X100级管线钢及其焊接性[J].焊接学报,2007(10):105-108. |
| [8] | 缪鹏飞,童彦刚,郭彦兵.超低碳贝氏体钢中合金元素的作用及其对焊接性的影响[J].热加工工艺,2010(20):29-32,35. |
| [9] | 张敏,吕金波,王超,李继红.一种X100管线钢埋弧焊丝的研究与开发[J].焊接学报,2011(01):1-4,8. |
| [10] | 顾纪清;阳代军.管道焊接技术[M].北京:化学工业出版社,2005:6. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%