对不同温度下的半固态ZA9合金凝固过程中的传热和流动行为进行模拟,测量出合金在不同工艺下的温度场分布,获取不同温度场下的金相图,并计算出其对应温度下的凝固率和晶粒的形状特征尺度.结果表明:温差较大的晶粒成型速度较快,合金的传热性较高;对合金采用机械振动和机械搅拌后,枝晶碎断,使晶粒大大细化,半固态合金内部的温度场分布趋于均匀,从而改善合金组织性能.
By simulating the heat transfer and flow behavior of ZA9 semi-solid alloy in solidification process at different temperature,temperature field distribution of the alloy in different process,and metallographic diagram at different temperatures were obtained,and the solidification rate and grain shape characteristic scale at corresponding temperature were calculated. The experimental results show that under the condition of larger temperature difference,the molding speed of grain is faster,thus the alloy has excellent heat transfer performance;After mechanical vibration and mechanical stirring,the dendritic crystal is broken off,grain refines,and the temperature field distribution in the semi?solid alloy tends to be homogeneous,thus improving microstructure and properties of alloy.
参考文献
| [1] | 张心明,王凌云,尚春民,杨建东.复摆法弹药静态多参数测试仪器研究[J].仪器仪表学报,2008(01):212-215. |
| [2] | Bipm-iec-ifcc-iso-iupap-oiml.Guide to expressio of uncertainy in measurement(GUM)[S].ISO,1995. |
| [3] | 顾强,李波.弹体质量、质心及质偏的新三点测量法[J].弹箭与制导学报,2005(04):177-178,201. |
| [4] | 金雪 .基于质量质心测量的称重仪数据采集及处理系统研制[D].哈尔滨工业大学,2010. |
| [5] | 薄悦 .提高质心测量灵敏度的关键技术研究[D].郑州:郑州机械研究所,2002. |
| [6] | 郑宾,侯文,杨瑞峰.大尺寸柱状结构质量、质心测量方法[J].测试技术学报,2002(02):108-111. |
| [7] | 卢志辉,孙志扬,李祥云,薄悦,张磊乐.高精度质心测量方法研究[J].兵工学报,2009(12):1748-1752. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%