采用无风电热干燥、真空干燥和冷冻干燥等3种方式处理生物纤维素凝胶膜,制备了3种生物纤维素膜(BC1、BC2、BC3),然后研究了其SEM形貌、IR、XRD和物理机械性能、孔隙率、吸液量、保液量、水蒸气透过率、透光率和热稳定性能.结果表明BC1的表面致密,BC2的孔洞和裂缝较BC1明显,BC3具有层状和孔洞结构.3种BC膜的晶型都是纤维素Ⅰ,但是BC1的结晶度为73.9％,BC2的结晶度为63.8％,BC3的结晶度为58.2％.BC1的弹性模量、断裂强度、透光率和热稳定性最好,BC3的孔隙率、吸液量、保液量和透湿性能最优异,BC2的各项性能处于BC1和BC3之间.
参考文献
| [1] | 刘四新;李从发.细菌纤维素[M].北京:中国农业大学出版社,2007:5-14. |
| [2] | 潘颖,朱平.细菌纤维素的理化特性及其应用开发[J].合成纤维,2007(09):6-10,18. |
| [3] | Yamanaka S;Ishihara M;Sugiyama J .[J].Cellulose,2000,7(03):213-225. |
| [4] | Nakagaito A N;Iwamoto S;Yano H .[J].Applied Physics A:Materials Science and Processing,2005,80(01):93-98. |
| [5] | Jaehwan Kim;Cai Zhijiang;Chen Yi .[J].Journal of Nanotechnology in Engineering and Medicine,2010,1(01):1-6. |
| [6] | Helenius G;Bacckdahl H;Bodin A .[J].Journal of Biomedical Materials Research,2006,76(02):431-438. |
| [7] | Grazyna Strobin;Andrzej Wlochowicz;Danuta Ciechanska;Stefan Boryniec;Henryk Struszczyk;Serafina Sobczak .GPC studies on bacterial cellulose[J].International Journal of Polymeric Materials,2004(10):889-900. |
| [8] | H. S. Barud;R. M. N. Assuncao;M. A. U. Martines .Bacterial cellulose-silica organic-inorganic hybrids[J].Journal of Sol-Gel Science and Technology,2008(3):363-367. |
| [9] | Moon S H;Park J M;Chun H Y et al.[J].Biotechnology and Bioprocess Engineering,2006,11(01):26-31. |
| [10] | Kanjanamosit, N;Muangnapoh, C;Phisalaphong, M .Biosynthesis and Characterization of Bacteria Cellulose-Alginate Film[J].Journal of Applied Polymer Science,2010(3):1581-1588. |
| [11] | Nge T T;Nogi M;Yano H et al.[J].Cellulose,17(02):349-363. |
| [12] | Ong-ard Saibuatong;Muenduen Phisalaphong .Novo aloe vera-bacterial cellulose composite film from biosynthesis[J].Carbohydrate Polymers: Scientific and Technological Aspects of Industrially Important Polysaccharides,2010(2):455-460. |
| [13] | 马霞,陈世文,王瑞明,陆大年,贾士儒.纳米材料细菌纤维素对大鼠皮肤创伤的促愈作用[J].中国临床康复,2006(37):45-47,插图37-3. |
| [14] | 谭玉静,洪枫,邵志宇.细菌纤维素在生物医学材料中的应用[J].中国生物工程杂志,2007(04):126-131. |
| [15] | Ramana KV;Ganesan K;Singh Lokendra .Pervaporation performance of a composite bacterial cellulose membrane: dehydration of binary aqueous-organic mixtures[J].World Journal of Microbiology & Biotechnology,2006(6):547-552. |
| [16] | 杜艳芳,陈彦,聂福德,裴重华.细菌纤维素在炸药环境中的酶解研究[J].含能材料,2007(06):583-586. |
| [17] | Nasrullah S;Jung H H;Joong K P .[J].Biotechnology and Bioprocess Engineering,2010,15(01):110-118. |
| [18] | 周伶俐,孙东平,吴清杭,杨加志,杨树林.不同培养方式对细菌纤维素产量和结构性质的影响[J].微生物学报,2007(05):914-917. |
| [19] | 潘颖 .细菌纤维素的制备及改性研究[D].青岛大学,2007. |
| [20] | 孙东平,杨加志,李骏,周伶俐,于俊伟.载银细菌纤维素抗菌敷料的制备及其抗菌性能的研究[J].生物医学工程学杂志,2009(05):1034-1038. |
| [21] | 刘长生 .细菌纤维素及其改性膜应用于医用敷料的初步研究[D].南京理工大学,2009. |
| [22] | 陶希芹,王明力,司方.纳米TiO2/壳聚糖复合膜的制备与性能研究[J].贵州工业大学学报(自然科学版),2008(04):158-163. |
| [23] | 周毓,刘艳.细菌纤维素研究进展[J].广州化工,2007(02):8-9. |
| [24] | 朱平.功能纤维及功能纺织品[M].北京:中国纺织出版社,2006:17. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%