研究了高速微粒轰击NiCoCrAlY粘结层后的热障涂层热生长氧化物(TGO)的生长过程.结果表明:等离子喷涂涂层1050℃×72h高温氧化后TGO出现明显分层现象,而经过高速微粒轰击涂层1050℃×96h高温氧化后TGO形貌更为平坦且无分层现象发生.此外,NiCoCrAlY粘结层经高速微粒轰击后产生大量的位错网;TGO进入稳态氧化阶段时间缩短,稳态氧化阶段时间延长.涂层抗高温氧化性能明显提高.
参考文献
| [1] | Zhou YC.;Tonomori T.;Yoshida A.;Liu L.;Bignall G.;Hashida T. .Fracture characteristics of thermal barrier coatings after tensile and bending tests[J].Surface & Coatings Technology,2002(2/3):118-127. |
| [2] | Leontiev S A;Kuznetsov V G;Rybnikov A I et al.Structure and properties of protective coating produced by vacuum arc deposition[J].Surfa Coat Tech,1995,76-77(13):41-46. |
| [3] | Rybnikov A I;Tchizhik A A;Ogurtsov A P et al.The structure and properties of metal and metal-ceramic coaings produced by physical vapour deposition[J].Journal of Materials Processing Technology,1995,55(34):234-241. |
| [4] | 向兴华,陈康年,刘正义,李尚周,尹钟大,朱景川,全成军.等离子喷涂ZrO2-NiCoCrAlY梯度涂层的成分分布与力学性能[J].复合材料学报,2000(01):89-92. |
| [5] | Nitin P. Padture;Maurice Gell;Eric H. Jordan .Thermal Barrier Coatings for Gas-Turbine Engine Applications[J].Science,2002(5566):280-284. |
| [6] | Nitin P. Padture;Maurice Gell;Eric H. Jordan .Thermal Barrier Coatings for Gas-Turbine Engine Applications[J].Science,2002(5566):280-284. |
| [7] | Li H W;Chang E;Wu B C et al.Effects of bond coatpreoxidation on the properties of ZrO2-8 wt% Y2O3/Ni22Cr10Al1Y thermal barrier coatings[J].Oxid Metal,1991,36(3/4):22-228. |
| [8] | 徐前岗,唐建新,王宁,陆峰,吴学仁.粘结层表面预处理对EB-PVD热障涂层循环氧化的影响[J].航空材料学报,2004(04):30-34. |
| [9] | 熊天英,刘志文,李智超,吴杰,金花子,李铁藩.超音速微粒轰击金属表面纳米化新技术[J].材料导报,2003(03):69-71. |
| [10] | 宋尽霞,韩雅芳,刘庆瑔,宫声凯,李树索,赵松.喷丸处理对IC6合金NiCoCrAlY涂层表面粗糙度的影响[J].航空材料学报,2006(03):289-290. |
| [11] | 李会谦,马江虹,任先京,于月光.热障涂层的氧化机理分析[J].有色金属（冶炼部分）,2007(z1):54-57. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%