研究了快淬作用对Ti-28V-15Mn-10Cr合金的相结构和储氢性能的影响.XRD实验结果表明,快淬处理使得合金由BCC和C14 Laves两相结构转变为单一的BCC相结构,同时合金的晶格常数随着快淬冷速的增加而增大.快淬作用能显著改善Ti-28V-15Mn-10Cr合金的吸放氢平台特性,从而导致合金放氢量的增加.然而,快淬处理也使得合金的放氢平台压下降以及活化性能变差.
参考文献
| [1] | Li Rong;Wu Jianmin;Wang Xinlin .[J].Journal of Alloys and Compounds,2000,311:40. |
| [2] | Au M;Pourarian F;Sankar S G;Wallace W E, Zang L .[J].Materials Science and Engineering B,1995,33:53. |
| [3] | 陈长聘,徐海鸥,王舷,陈立新.V+TiFe0.85Mn0.15复相合金的储氢特性[J].稀有金属材料与工程,2003(04):291-294. |
| [4] | 陈长聘,耿伟贤,陈昀,王启东.Ti-Zr-Mn-M（M=Cr,V或Cr与V）合金的储氢性能和晶体结构[J].稀有金属材料与工程,2001(01):31-34. |
| [5] | Wang Lianbang;Tang Yuanhua;Wang Yijing;Li Qiudi , et al.[J].Journal of Alloys and Compounds,2002,336:297. |
| [6] | Iba H;Akiba E .[J].Journal of Alloys and Compounds,1997,253:21. |
| [7] | Iba H;Akiba E .[J].Journal of Alloys and Compounds,1995,23:508. |
| [8] | Akiba E;Iba H .[J].Intermetallics,1998,6:461. |
| [9] | Okada M;Kuriiwa T;Tamura T et al.[J].Journal of Alloys and Compounds,2002,330～332:511. |
| [10] | Okada M.;Kuriiwa T.;Kamegawa A.;Takamura H. .Role of intermetallics in hydrogen storage materials[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(0):305-312. |
| [11] | Zhang LY .[J].Journal of Alloys and Compounds,1999,621～625:293. |
| [12] | Li Chunajian;Wang Xinlin;Wang Chongyu .[J].Journal of Power Sources,1998,74:62. |
| [13] | Yu Xuebin;Wu Zhu;Huang Taizhong;Chen Jingzhou , et al.[J].Journal of Materials Research,2003,18:2553. |
| [14] | Yu Xuebin;Wu Zu;Huang Taizhong;Cheng Jinzhou , et al.[J].Materials Chemistry and Physics,2004,83:273. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%