采用W,C,Co粉末为原料,通过机械活化-反应热处理工艺制备出晶粒尺寸为30.5 nm的WC-Co复合粉末.研究发现该工艺具有以下特征:反应温度低,反应速度快.在800℃热处理时已有大量的WC生成.在850℃保温25min,W2C就完成了向WC的转化.经900℃保温35 min制得纳米晶粒WC-Co复合粉末.
参考文献
| [1] | 高海燕,曹顺华.机械合金化制备纳米晶硬质合金粉的进展[J].粉末冶金技术,2003(06):355-358. |
| [2] | 王辉平,胡茂中.纳米技术与硬质合金[J].中国钨业,2001(02):30-32. |
| [3] | Wang Xingqing;Chen Lidong;Li Xiaodong et al.[J].Materials Research Innovations,2005,9(03):82. |
| [4] | Lisovsky A F .[J].J of Refractory Metals and Hard Materials,2003,21(1-2):63. |
| [5] | Engqvist H;Uhrenius B .[J].J of Refractory Metals and Hard Materials,2003,21(1-2):31. |
| [6] | Engqvist H;Jacobson S .[J].Wear,2002,252(5-6):384. |
| [7] | Andren Hans-Olof .[J].Materials & Design,2001,22(06):491. |
| [8] | Davis R M;McDermott B;Koch C C .[J].Metallurgical Transactions,1998,19A:2867. |
| [9] | Cha SI.;Hong SH.;Kim BK. .Spark plasma sintering behavior of nanocrystalline WC-10Co cemented carbide powders[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):31-38. |
| [10] | Cha Seung I;Kim Byung K;Hong Soon H .[J].Rare Metals,2002,21:130. |
| [11] | 席生岐;屈晓燕;刘心宽 .[J].材料科学与工程,2000,8(03):88. |
| [12] | 刘寿荣 .[J].硬质合金,1997,14(04):198. |
| [13] | Lee G H;Kang S .[J].Materials Transactions,2001,42(08):1575. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%