用四种不同方法处理芳纶浆粕(以下简称AP),并制备成三元乙丙橡胶(EPDM)复合材料,分析其力学、烧蚀性能和残炭结果.结果表明,未改性的AP在加入超过6份时分散能力变差,性能下降.而通过硅烷偶联剂改性的AP,增加AP用量的同时,既能改善分散能力,又可以提高样品残炭量、炭层的稳固性.热重分析(TGA)残炭量由30.4%提高到33.9%(898.6℃),线烧蚀率也降低了31.6%.无机粉体处理AP虽能改善其在胶体的分散能力,但由于无机粉体与有机相的结合能力不好,导致改性AP对力学和烧蚀性能改善效果不明显.
参考文献
| [1] | R.S. Rajeev;S.K. De;Anil K. Bhowmick;Baby John .Studies on thermal degradation of short melamine fibre reinforced EPDM, maleated EPDM and nitrile rubber composites[J].Polymer Degradation and Stability,2003(3):449-463. |
| [2] | J.Maity;C.Jacob;C.K.Das .Fluorinated Aramid Fiber Reinforced Polypropylene Composites and Their Characterization[J].Polymer Composites,2007(4):462-469. |
| [3] | C.W.Tsimpris;J.Wartalski .Compounding with para-aramid fiber engineered elastomers[J].Rubber World: The Technical Service Magazine for The Rubber Industry,2001(1):35-40. |
| [4] | Rubber World Group .Engineered elastomer for reinforcement[J].Rubber World: The Technical Service Magazine for The Rubber Industry,2005(3):28-30,32-36-0. |
| [5] | 黄良仙,安秋凤,李临生.抗静电剂及其在工业领域的应用[J].日用化学工业,2004(05):308-311. |
| [6] | 胡广君,钱建明,张立群,吴湘娟,白健.新型橡胶填料--空心玻璃微珠[J].特种橡胶制品,2002(06):14-17. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%