Constant load creep tests on isothermally forged Udimet 720Li, an advanced superalloy for gas turbine disc application, were run in the stress/temperature field 900-450MPa/650-700℃ producing rupture times in the 20-5000h range.The creep curves have shown a predominant accelerating creep stage, that has been described by the following equation:ε=εmin (σ,T) [ 1 +C(σ)ε ] where εmin depends on stress and temperature, while parameter C depends mainly on stress.A strain dependent damage, defined by the parameter C, causes the accelerating creep stage at stresses lower than 750MPa, whilst its contribution to the creep strain acceleration is less important at higher stresses.The model rationalizes the different behaviors at high and low stress and has been validated with variable stress and temperature creep behavior.
参考文献
| [1] | G.W.Konig;Elsevier Sci;K-T.Rie;P.D.Portella.in Proc.of the Low Cycle Fatigue and Elasto-Plastic Behavior of Materials[M].Amsterdam,The Netherlands,1998:807. |
| [2] | M.P.Jackson;R.C. Reed .Heat treatment of UDIMET 720Li the effect of microstructure on properties[J].Materials science and engineering,1999(1):85-97. |
| [3] | M.Maldini;V.Lupinc;R.Townsend;M.Winstone, M.Henderson, J.R.Nicholls, A.Partridge, B.Nath.M.Wood R.Viswanathan.in Proc.of the Life Assessment of Hot Section Gas Turbine Components[C].IOM Comunications,London,UK,2000:109. |
| [4] | S Dubiez-Le Goff;R Couturier;L Guetaz;H.Burlet .[J].Materials Science and Engineering A,2004,387-389:599. |
| [5] | V Lupinc;L Z Zhou;M.Maldini .Proc.of EUROMAT 2001,Paper No.394[R].AIM,Milan,Italy,2001. |
| [6] | M.Maldini;V.Lupinc.[J].Scripta Metallurgica et Materialia:1737. |
| [7] | M.Maldini;V.Lupinc.[J].Scripta Metallurgica et Materialia:337. |
| [8] | B.F.Dyson;M.Mclean .[J].Acta Materialia,1983,31:17. |
| [9] | B.F.Dyson;T.B.Gibbons .[J].Acta Materialia,1987,35:2355. |
| [10] | A Barbosa;N·G·Taylor;M·F·Ashby;B.F.Dyson M.McLean, D.N.Duhl, G.Maurer, S.Antolovich, C.Lund S.Reichman.in Proc.of the 6th International Symposium on Superalloys[M].Metall.Soc.A.I.M.E.;New York,1988:683. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%