以ZrH_2为发泡剂,采用熔体发泡法制备铝基小孔径泡沫铝,分析其制备过程及影响孔结构的因素;优化实验室制备泡沫铝的工艺条件;借助图形分析方法表征泡沫铝的孔径分布,并与TiH_2制备的泡沫铝进行了对比;采用改进座滴装置研究铝合金与氢化物的润湿行为.结果表明:ZrH_2较适合制备小孔径泡沫铝;优化工艺条件为:Al 650 g,增粘剂Ca 的加入量2.5%,发泡剂ZrH_2的加入量1.0%,发泡温度680 ℃,搅拌时间1.5 min,保温时间2.5 min;制备的泡沫铝孔径均匀,平均孔径小于1.5 mm;ZrH_2在铝合金中的润湿特点是导致泡沫铝孔径较小的主要原因.
Foam aluminum with small pore diameters was prepared by the melt-based route using ZrH_2 as foaming agent. The relationship between the foaming process parameters and the cell structures of foam aluminum was studied. The foaming process conditions were optimized. The pore diameter distribution of the foam aluminum was characterized by the graphical analysis method and the foaming agent TiH_2 was commonly used for the comparison. The improved sessile drop device was used to research the wetting behaviors of Al alloy on the surface of hydride. The results indicate that the foaming agent ZrH_2 is suitable for preparation of the small pore diameter foam aluminum and the optimized process conditions are obtained (650 g of Al; addition of Ca 2.5%; ZrH_2 1.0%; temperature 680 ℃; stirring time 1.5 min; holding time 2.5 min). The average pore diameter is uniform and below 1.5 mm. The wetting behaviors are the main factor of influencing the pore diameter.
参考文献
[1] | John Banhart .Manufacture, characterization and application of cellular Metals and metal foams[J].Progress in materials science,2001(6):559-632. |
[2] | F. von Zeppelin;M. Hirscher;H. Stanzick .Desorption of hydrogen from blowing agents used for foaming metals[J].Composites science and technology,2003(16):2293-2300. |
[3] | I.Duarte;J.Banhart .A Study of Aluminium Foam Formation—Kinetics and Microstructure[J].Acta materialia,2000(9):2349-2362. |
[4] | V. Gergely;D. C. Curran;T. W. Clyne .The FOAMCARP process: foaming of aluminium MMCs by the chalk-aluminium reaction in precursors[J].Composites science and technology,2003(16):2301-2310. |
[5] | Zhen-lun Song;Jin-song Zhu;Li-qun Ma;De-Ping He .Evolution of foamed aluminum structure in foaming process[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1/2):137-143. |
[6] | Matijasevic-Lux B;Banhart J;Fiechter S;Gorke O;Wanderka N .Modification of titanium hydride for improved aluminium foam manufacture[J].Acta materialia,2006(7):1887-1900. |
[7] | A. R. Kennedy .The effect of TiH_2 heat treatment on gas release and foaming in Al-TiH_2 performs[J].Scripta materialia,2002(11):763-767. |
[8] | 方吉祥,杨志懋,丁秉钧.SiO2/TiH2包覆粉体的制备及其释氢特性[J].高等学校化学学报,2005(07):1225-1227. |
[9] | 周向阳,张华,刘希泉,刘宏专.泡沫铝两步法制备工艺用新型发泡剂的热分解行为[J].中国有色金属学报,2008(12):2265-2269. |
[10] | 严富学,赵康,谷臣清.用新型发泡剂--氢化混合稀土制备泡沫铝的研究[J].中国稀土学报,2005(02):186-189. |
[11] | I. Mukai;T. Miyoshi;S. Nakano .Compressive Response of a Closed-Cell Aluminum Foam at High Strain Rate[J].Scripta materialia,2006(4):533-537. |
[12] | UENO H;AKIYAMA S .Effects of calcium addition on the foamability of molten aluminum (in Japanese)[J].Light Metals,1987,37(01):42-47. |
[13] | 李兵,姚广春,王永,罗洪杰.纯铝基泡沫铝材料的制备工艺[J].东北大学学报(自然科学版),2007(08):1159-1162. |
[14] | Y.Q. SUN;T. GAO .The Optimum Wetting Angle for the Stabilization of Liquid-Metal Foams by Ceramic Particles: Experimental Simulations[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2002(10):3285-3292. |
[15] | 任俊;沈健;卢寿慈.颗粒分散科学与技术[M].北京:化学工业出版社,2005:204-207. |
[16] | 何继敏.新型聚合物发泡材料及技术[M].北京:化学工业出版社,2008:9-12. |
[17] | 吴林丽,姚广春,罗天骄,张晓明.镁对铝与粉煤灰润湿性的影响[J].中国有色金属学报,2004(10):1700-1704. |
[18] | Ping Shen;Hidetoshi Fujii;Kiyoshi Nogi .Wettability of polycrystalline rutile TiO_2 by molten Al In different atmospheres[J].Acta materialia,2006(6):1559-1569. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%